Precision Grinding of SUS304 Using Metal Bonded CBN Wheel
Precision Grinding of SUS304 Using Metal Bonded CBN Wheel
复制标题
DOI：
10.4028/www.scientific.net/amr.24-25.261
复制
发表时间：
2007-09
期刊：
影响因子：
--
通讯作者：
Y. Hasuda;Y. Suzuki;Y. Tadokoro;S. Kinebuchi;T. Ohashi;T. Furusawa
中科院分区：
文献类型：
--
作者：
Y. Hasuda;Y. Suzuki;Y. Tadokoro;S. Kinebuchi;T. Ohashi;T. Furusawa
进行了耐磨性优良的金属结合剂CBN砂轮磨削不锈钢的基础试验。通过对砂轮磨损过程和磨削后表面质量的分析，得出了最适宜的磨削条件。磨削至7000mm~3/mm时，砂轮的径向磨损量为3μm，表面粗糙度Rz小于等于0.5μm。磨削比Gr达到3000左右，实现了表面粗糙度变化不大的长寿命磨削。
The fundamental experiment of the grinding of the stainless steel using the metal bonded CBN wheel which was excellent in wear resistance was conducted. The most appropriate grinding conditions were obtained by clarifying wear process of grinding wheel and finished ground surface quality. When grinding was carried out up to stock removal 7000mm3/mm, radial wear of grinding wheel %R is 3μm and surface roughness Rz was 0.5μm or less. The grinding ratio Gr becomes about 3000, and long life grinding with little change of surface roughness was possible.