Magnetic properties of Sm5Fe17 melt-spun ribbon
Magnetic properties of Sm5Fe17 melt-spun ribbon
复制标题
Sm5Fe17熔纺带材的磁性能
DOI：
10.1063/1.2711397
复制
发表时间：
2007
期刊：
影响因子：
--
通讯作者：
T. Saito
中科院分区：
文献类型：
--
作者：
T. Saito
研究了Sm5Fe17熔纺带的结构与磁性能的关系。非晶态Sm5Fe17熔纺带退火后得到的熔纺带由在973K下退火0h（即加热后立即关闭炉）的Sm5Fe17相和在973K下退火1h的Sm5Fe17相和少量SmFe12相组成。退火后Sm-Fe熔纺带的矫顽力与退火条件密切相关。退火后Sm5Fe17熔纺带的最大矫顽力超过36kOe。
The relationship between the structures and magnetic properties of Sm5Fe17 melt-spun ribbons was studied. The melt-spun ribbons obtained by annealing of amorphous Sm5Fe17 melt-spun ribbon consisted of the Sm5Fe17 phase when annealed at 973K for 0h (i.e., when the furnace was immediately turned off after heating) or the Sm5Fe17 phase together with a small amount of the SmFe12 phase when produced by annealing at 973K for 1h. The coercivity of the annealed Sm–Fe melt-spun ribbons was strongly dependent on the annealing conditions. The maximum coercivity of the annealed Sm5Fe17 melt-spun ribbons exceeded 36kOe.
影响因子：
3.2
作者：
SAGAWA, M;FUJIMURA, S;MATSUURA, Y
通讯作者：
MATSUURA, Y