Hot compressive deformation behavior and electron backscattering diffraction analysis of Mg95.50Zn3.71Y0.79 fine-grained alloy solidified under high pressure
Hot compressive deformation behavior and electron backscattering diffraction analysis of Mg95.50Zn3.71Y0.79 fine-grained alloy solidified under high pressure
复制标题
Mg95.50Zn3.71Y0.79细晶合金高压凝固热压缩变形行为及电子背散射衍射分析
DOI：
10.1007/s10853-017-1698-x
复制
发表时间：
2018-02
影响因子：
4.5
通讯作者：
Wang Lin
中科院分区：
文献类型：
--
作者：
Fan Zhibin;Lin Xiaoping;Dong Yun;Xu Rui;Wang Lin
Mg95.50Zn3.71Y0.79通过高压凝固制备了晶粒尺寸为16 μm的细晶凝固合金。比较了该合金在高压下凝固的组织特征和热压缩变形行为，
An Mg95.50Zn3.71Y0.79 fine-grained solidified alloy with a grain size of 16 μm was prepared by high-pressure solidification. The microstructure characteristics and hot compressive deformation behavior of the alloy solidified under high pressure were compa
登录
查看更多内容
影响因子：
17.6
作者：
Kai Wen;Ke Liu;Zhaohui Wang;Shu-bo Li;W. Du
通讯作者：
Kai Wen;Ke Liu;Zhaohui Wang;Shu-bo Li;W. Du
DOI：
10.1016/j.msea.2008.02.053
发表时间：
2009-03
影响因子：
6.4
作者：
Manping Liu;H. Roven;M. Murashkin;R. Valiev
通讯作者：
Manping Liu;H. Roven;M. Murashkin;R. Valiev
影响因子：
2.3
作者：
林小娉;董允;徐瑞;孙桂芳;焦世辉
通讯作者：
林小娉;董允;徐瑞;孙桂芳;焦世辉
影响因子：
8.4
作者：
N. Tahreen;Dingfei Zhang;F. Pan;X. Jiang;Dongyang Li;Daolun L. Chen
通讯作者：
N. Tahreen;Dingfei Zhang;F. Pan;X. Jiang;Dongyang Li;Daolun L. Chen
影响因子：
8.4
作者：
Nali Li;G. Huang;X. Zhong;Qing Liu
通讯作者：
Nali Li;G. Huang;X. Zhong;Qing Liu