Improve Uniformity of the Cores and Je of Bi-2212 Wires
Improve Uniformity of the Cores and Je of Bi-2212 Wires
复制标题
DOI：
10.1016/j.phpro.2014.09.036
复制
发表时间：
2014
期刊：
影响因子：
--
通讯作者：
Q. Hao;C. Li;Shengnan Zhang;G. Li;L. Bai;L. Guoqing;X. Xiong;P. Zhang
中科院分区：
文献类型：
--
作者：
Q. Hao;C. Li;Shengnan Zhang;G. Li;L. Bai;L. Guoqing;X. Xiong;P. Zhang
At low temperature and high field, Bi-2212 wires have the highest critical current density (Jc), and the isotropic round wires are more easily to design solenoid than the tapes. So the Bi-2212 wires are the preferred conductor for high-field solenoids. If theJcof Bi-2212 wires was highest, the diameter of core of the wires was about 20 μm. It is so thin that some cores were broken by inhomogeneous force. So it was important for Bi-2212 wires to deform uniformly during the drawing. Effect of technological parameters on the Uniformity and the engineering critical current density (Je) were studied. The results showed that the reduction per pass affected the Uniformity andJeof Bi-2212 wires. If the reduction per pass was too small, there were only a local deformation and the unfavourable stress-strain distribution could found in the transverse section of the wires. When the reduction per pass was large enough, there was a synchronous deformation of each part of the wires. So the uniformity of sample with large reduction per pass was better than that of sample with small reduction per pass. ItsJevalue was also higher than that of sample with small reduction per pass with the same diameter and there were the higher maximumJevalue for it. When it was the smaller diameter, the sample with large reduction per pass reached to the maximumJe. 20 percent of reduction per pass basically met the requirement of the synchronous deformation and highJeof Bi-2212 wires.