Enhancing the pinning strengths in polycrystalline MgB2
Enhancing the pinning strengths in polycrystalline MgB2
复制标题
DOI：
10.1002/crat.200800441
复制
发表时间：
2009-03
影响因子：
1.5
通讯作者：
I. Obaidat;B. Albiss;M. Gharaibeh;M. Hasan
中科院分区：
文献类型：
--
作者：
I. Obaidat;B. Albiss;M. Gharaibeh;M. Hasan
The dependence of the critical current density, Jc, on the gamma irradiation dose in MgB2 polycrystalline superconducting specimens has been studied. The MgB2 samples were irradiated with 10 MR and 20 MR doses of γ‐rays. The critical current density, Jc was found to be enhanced almost at all temperatures after irradiation. The enhancement of Jc was found to be linear with the irradiation dose at all temperatures. We also report on the correlation between the superconducting transition temperature and the residual resistivity ratio. Most of our results agree with the Testardi and Mooij rules which suggest that the dominant pairing mechanism of MgB2 is the phonon‐mediated interaction. (© 2009 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)