High-temperature ex-vessel corium spreading. Part 1: experimental investigations on ceramic and sacrificial concrete substrates
High-temperature ex-vessel corium spreading. Part 1: experimental investigations on ceramic and sacrificial concrete substrates
复制标题
高温血管外真皮扩散。
DOI：
10.1080/00223131.2021.1977199
复制
发表时间：
2021
影响因子：
1.2
通讯作者：
C. Journeau
中科院分区：
文献类型：
--
作者：
Michael Johnson;A. Denoix;V. Bouyer;H. Goda;S. Kamohara;J. Takeuchi;L. Brissonneau;C. Journeau
Please try later.
ABSTRACT Optimizing melt spreading in the aftermath of a core disruptive accident is crucial for achieving sufficient melt cooling to maintain reactor containment integrity. Two ≈30 kg-scale experiments performed at the VULCANO facility explore the spreading of high-temperature molten corium-concrete mixtures over ceramic and sacrificial concrete substrates. Imaging of the melt front propagation revealed a 7% increase in spreading length and a 30% increase in maximum front velocity during spreading over sacrificial concrete, despite a reduced mass partaking in spreading due to increased holdup within the crucible. Infrared imaging of the melt indicated surface temperatures around 45°C lower during spreading on sacrificial concrete, resulting in a roughly three-fold increase in melt viscosity. The enhanced viscosity and reduced mass during the VE-U9-concrete test imply an increased spreadability on sacrificial concrete greater than the observed 7% increase in spreading length. This enhanced spreadability on sacrificial concrete could be explained by the apparent gliding motion of the melt, consistent with reduced friction at the melt-substrate interface. Reduced friction at the melt-substrate interface is best explained by a diphasic film of molten concrete and gaseous concrete decomposition products acting as a lubricant between the melt and solid substrate.