Adjustable Zero Thermal Expansion in Antiperovskite Manganese Nitride
Adjustable Zero Thermal Expansion in Antiperovskite Manganese Nitride
复制标题
反钙钛矿氮化锰的可调零热膨胀
DOI：
10.1002/adma.201102552
复制
发表时间：
2011-10-25
影响因子：
29.4
通讯作者：
Yin, Fuxing
中科院分区：
文献类型：
--
作者：
Song, Xiaoyan;Sun, Zhonghua;Yin, Fuxing
发现了控制反钙钛矿氮化锰零热膨胀（ZTE）行为的通用机制。调节其晶格位置处的锰占据量会导致热膨胀行为发生巨大变化。通过对材料进行纳米结构处理，可以减少锰位点的占用，从而产生“巨型”ZTE 的形式。
A universal mechanism that controls the zero thermal expansion (ZTE) behavior of the antiperovskite manganese nitrides is discovered. Modulating the Mn occupancy at its lattice sites leads to a drastic change in the thermal expansion behavior. The Mn site occupancy can be reduced by nanostructuring the material, generating a form of "giant" ZTE.