以纳米镍为催化剂，在不同反应温度下催化裂解乙炔制备了不同形貌的纳米碳纤维。实验结果表明，温度是控制碳纤维尺寸和形态的关键参数。在400 °C下形成从镍颗粒发出的双螺旋纤维和线性分叉纤维;而在450 °C、500 °C和550 °C的反应温度下仅获得线性碳纳米纤维。在低温下，镍纳米颗粒保留在两根纤维的中间，而在高温下，镍颗粒位于线性纤维的一端。
Carbon nanofibers with various morphologies were synthesized by the catalytic pyrolysis of acetylene using nickel catalyst nanoparticles at different reaction temperatures. Experimental results demonstrate that temperature is a critical parameter for controlling the size and morphology of carbon fibers. Twin coiled fibers and linearly bifurcating fibers emanating from nickel particles were formed at 400 °C; whereas, only linear carbon nanofibers were obtained at reaction temperatures of 450 °C, 500 °C, and 550 °C. At low temperatures, nickel nanoparticles remain in the middle of two fibers, while nickel particles are positioned at one end of the linear fibers at high temperatures.
登录
查看更多内容
影响因子：
4
作者：
L. Zhang;A. Melechko;V. Merkulov;M. Guillorn;M. Simpson;D. Lowndes;M. Doktycz
通讯作者：
L. Zhang;A. Melechko;V. Merkulov;M. Guillorn;M. Simpson;D. Lowndes;M. Doktycz
影响因子：
64.8
作者：
IIJIMA, S
通讯作者：
IIJIMA, S
氢弧等离子体法制备铁纳米颗粒，乙炔热解催化合成碳纳米纤维和纳米管
影响因子：
3
作者：
通讯作者：
--
影响因子：
3.3
作者：
S. Takenaka;M. Ishida;M. Serizawa;E. Tanabe;K. Otsuka
通讯作者：
S. Takenaka;M. Ishida;M. Serizawa;E. Tanabe;K. Otsuka
DOI：
10.1016/0965-9773(96)00006-2
发表时间：
1996-03
期刊：
Nanostructured Materials
影响因子：
--
作者：
Z. Cui;Zhikun Zhang
通讯作者：
Z. Cui;Zhikun Zhang