アルミナ粒子分散型Al-Cu-Mg合金基複合材料の時効挙動に及ぼす粒子体積率の影響
アルミナ粒子分散型Al-Cu-Mg合金基複合材料の時効挙動に及ぼす粒子体積率の影響
复制标题
颗粒体积分数对氧化铝颗粒弥散Al-Cu-Mg合金基复合材料时效行为的影响
DOI：
10.2464/jilm.43.465
复制
发表时间：
1993
期刊：
影响因子：
--
通讯作者：
静夫 多々
中科院分区：
文献类型：
--
作者：
進 池野;克彦 堀江;健二 松田;保裕 上谷;博之 穴田;静夫 多々
Aging behavior of alumina particle dispersed Al-Cu-Mg alloy composite materials containing various amount of alumina, was investigated by means of Vickers micro hardness test and transmission electron microscopy. GPB zone and S' intermediate precipitates were observed on aging at 423K in 2 vol%Al2O3/Al-Cu-Mg composite material, while GP zone and θ' intermediate precipitates appeared at the same aging condition in 6 and 8 vol%Al2O3/Al-Cu-Mg composite materials. A plolonged aging time was needed to reach a maximum hardness with increasing Al2O3 content. The maximum hardness decreased with increasing Al2O3 content in the case where the GPB zone and S'intermediate phases coexisted. On the other hand, in the case where GP zone and θ' intermediate phase coexisted, the values of maximum hardness were almost independent of Al2O3 content. At aging temperature of 473K, almost all precipitates were S' intermediate phase in 2 and 4 vol%Al2O3/Al-Cu-Mg composite materials. In these specimens, almost same and relatively shorter time was needed to reach a maximum hardness. While, in 6 and 8 vol%Al2O3/Al-Cu-Mg composite materials in which θ' intermediate phase exists, the maximum hardness values were lowered and longer aging time was needed.