Effect of W powders characteristics on the Ti-rich phase and properties of W-10 wt.% Ti alloy
Effect of W powders characteristics on the Ti-rich phase and properties of W-10 wt.% Ti alloy
复制标题
效果%20of%20W%20粉%20特性%20on%20the%20Ti富%20相%20and%20性能%20of%20W-10%20wt.%%20Ti%20合金
DOI：
10.1016/j.ijrmhm.2015.02.003
复制
发表时间：
2015-05-01
影响因子：
3.6
通讯作者：
Yang, Qing
中科院分区：
文献类型：
--
作者：
Dai, Weili;Liang, Shuhua;Yang, Qing
To obtain W-Ti alloy with less Ti-rich solid solution, W powders were modified by high-energy ball milling to increase their microdefects and accelerate diffusion of Ti in W. Bulk W-10 wt.% Ti alloy was also fabricated using milled/unmilled W powders and TiH2 powders by solid sintering. XRD, SEM and TEM were used to study the effect of ball milling of W powders on the formation of Ti-rich phase and properties of W-Ti alloy. The results showed that the defects of W powders were successfully induced by ball milling, the grain boundary increased due to the grain refinement and the dislocation density increased by 100 times comparing to the unmilled powders. The milling effect still retained at elevated temperature. On the basis of the above results, the diffusion of Ti into W was promoted and the generation probability of Ti-rich phase was inhibited with its phase content reducing from 16.7% to 12.7%, which can be interpreted in terms of the improvement in interdiffusion coefficient of W-Ti alloy by 40 times. The physical properties such as microhardness and electrical conductivity of W-Ti alloy were also improved evidently. (C) 2015 Elsevier Ltd. All rights reserved.