Phase Transformation Kinetics of High Nb-TiAl Alloy during Continuous Heating
Phase Transformation Kinetics of High Nb-TiAl Alloy during Continuous Heating
复制标题
高铌钛铝合金连续加热过程中的相变动力学
DOI：
10.1088/1742-6596/2133/1/012029
复制
发表时间：
2021-11
期刊：
影响因子：
--
通讯作者：
Jianxiu Liu
中科院分区：
文献类型：
--
作者：
Ying Li;Lian Zhou;Junpin Lin;Hui Chang;Jianglei Fan;Yang Cao;Yan Wang;Yongbiao Wang;Jianxiu Liu
抽象。本文利用透射电镜和光学显微镜研究了Ti-45 Al-8.5 Nb-（W，B，Y）合金在连续加热过程中的相变行为。结果表明，高Nb-TiAl合金在连续加热过程中的相变过程包括有序α2 →无序α和四角γ →六角α两个阶段。显微组织分析表明，在加热过程中，原始α2/γ层状组织转变为块状γ相和α相（以α2形式保留）。α2 → α和γ → α反应的活化能分别为989.65kJ/mol和995.30kJ/mol。此外，升温速率越低，相变达到平衡状态的速度越快。
Abstract. In this work, the phase transformation behavior of Ti-45Al-8.5Nb-(W, B, Y) alloy during continuous heating was investigated using dilatometer and optical microscopy. Results indicated that the phase transformation process of high Nb-TiAl alloy during continuous heating included two stages: ordered α2 → disorder α and tetragonal γ → hexagonal α. According to the microstructure analysis, the initial α2/γ lamellar structure transformed into the massive γ phase and α phase (retained as α2) during the heating process. The activation energy of α2 → α and γ → α was 989.65 kJ/mol and 995.30 kJ/mol, respectively. Moreover, the lower the heating rate was, the faster the phase transformation reached the equilibrium state.
登录
查看更多内容
影响因子：
6
作者：
M. Pérez-Bravo;I. Madariaga;K. Ostolaza;M. Tello
通讯作者：
M. Pérez-Bravo;I. Madariaga;K. Ostolaza;M. Tello
影响因子：
3.5
作者：
S. Hasani;M. Shamanian;A. Shafyei;P. Behjati;J. Szpunar
通讯作者：
S. Hasani;M. Shamanian;A. Shafyei;P. Behjati;J. Szpunar
影响因子：
6.2
作者：
Ying Li;Lian Zhou;Junpin Lin;Hui Chang;Lina Feng
通讯作者：
Ying Li;Lian Zhou;Junpin Lin;Hui Chang;Lina Feng
影响因子：
9.4
作者：
G. Ren;C. Dai;W. Mei;Jian Sun-;S. Lu;L. Vitos
通讯作者：
G. Ren;C. Dai;W. Mei;Jian Sun-;S. Lu;L. Vitos
TiAl 合金中通过马氏体相变细化微观结构
影响因子：
6.2
作者：
Chen Lin;Lin Junpin;Xu Xiangjun;Li Chan;Xu Yong;Liang Yongfeng
通讯作者：
Liang Yongfeng