Accelerated formation of sodium depletion layer on soda lime glass surface by corona discharge treatment in hydrogen atmosphere
Accelerated formation of sodium depletion layer on soda lime glass surface by corona discharge treatment in hydrogen atmosphere
复制标题
氢气氛下电晕放电处理加速钠钙玻璃表面贫钠层的形成
DOI：
10.1016/j.apsusc.2014.02.024
复制
发表时间：
2014
影响因子：
6.7
通讯作者：
Junji Nishii
中科院分区：
文献类型：
--
作者：
Keiga Kawaguchi;Hiroshi Ikeda;Daisuke Sakai;Shiro Funatsu;Keiichiro Uraji;Kiyoshi Yamamoto;Toshio Suzuki;Kenji Harada;Junji Nishii
在h2o2气氛下，电晕放电处理能有效地加速钠石灰玻璃表面钠耗尽层的形成。这种加速的一个原因是在阳极针端以较低的施加电压产生比在空气中具有更大迁移率的H+。第二个原因是电晕放电处理过程中施加在玻璃板上的电压，理论上估计是空气中电压的2.7倍。这两种作用使损耗层厚度比空气中的损耗层厚度增加了一倍。
Formation of a sodium depletion layer on a soda lime glass surface was accelerated efficiently using a corona discharge treatment in H2atmosphere. One origin of such acceleration was the preferential generation of H+with a larger mobility at an anode needle end with a lower applied voltage than that in air. The second origin was the applied voltage across the glass plate during the corona discharge treatment, which was estimated theoretically as 2.7 times higher than that in air. These two effects doubled the depletion layer thickness compared with that in air.
登录
查看更多内容
影响因子：
1.5
作者：
Xueming Liu;Mingde Zhang
通讯作者：
Mingde Zhang
使用电晕充电处理在玻璃基板上复制自组装粒子的衍射结构
影响因子：
1.2
作者：
D.Sakai;D.Miho;K.Harada;D.Barada;T.Fukuda
通讯作者：
T.Fukuda
影响因子：
3.5
作者：
LEPIENSKI, CM;GIACOMETTI, JA;ACHETE, CA
通讯作者：
ACHETE, CA
同心半球之间氢电晕放电中离子种类的测定
DOI：
10.1088/0022-3727/5/6/412
发表时间：
1972
期刊：
Journal of Physics D
影响因子：
--
作者：
D. Mellor;J. Travis
通讯作者：
J. Travis
使用红外光谱法定量硅酸盐玻璃中的 H2O 含量：基于卡尔费休滴定法分析的水合玻璃的校准
DOI：
--
发表时间：
2003
期刊：
影响因子：
--
作者：
H. Behrens;A. Stuke
通讯作者：
A. Stuke