Effect of Slag Composition on the Deoxidation and Desulfurization of Inconel 718 Superalloy by ESR Type Slag Without Deoxidizer Addition
Effect of Slag Composition on the Deoxidation and Desulfurization of Inconel 718 Superalloy by ESR Type Slag Without Deoxidizer Addition
复制标题
炉渣成分对不加脱氧剂ESR型炉渣脱氧脱硫Inconel 718高温合金的影响
DOI：
10.1007/s11663-019-01729-3
复制
发表时间：
2020-02-01
影响因子：
3
通讯作者：
Guo, Jing
中科院分区：
文献类型：
--
作者：
Duan, Sheng-Chao;Shi, Xiao;Guo, Jing
Effects of slag composition and alloy content as well as temperature on the deoxidation and desulfurization of Inconel 718 superalloy by CaF2-CaO-Al2O3-MgO-TiO2 ESR-type slag without the addition of a deoxidizer were systematically investigated by laboratory-scale experiments and the developed mass transfer model. The model predictions were verified through comparison with experimental results in a double-layer crucible. The results showed that the oxygen content decreased with an increase of CaO, MgO and CaF2 content in the slag at 1773 K, and CaO has a great influence on the deoxidation of Inconel 718 alloy compared with MgO and CaF2 in slag, which was responsible for the decrease in equilibrium content of sulfur in the Inconel 718 alloy. The total oxygen and sulfur content decreased from 33.2 and 20 ppm in master alloys to about 10 and 6 ppm in alloy ingots at 1773 K, respectively. Properly increasing the Al and Ti content only lowered the oxygen and sulfur content in the nickel-based alloy to a limited extent when satisfying the mechanical properties of the Inconel 718 alloy. The interfacial oxygen content increased with increasing temperature, giving rise to a decrease in the desulfurization ratio [pct S]t=t/[pct S]t=0. These results show that the lower temperature favored desulfurization of the nickel-based alloy.