Thermal Analysis of Calcium–Magnesium–Alumino–Silicate Infiltration Dynamics in Thermal Barrier Coatings
Thermal Analysis of Calcium–Magnesium–Alumino–Silicate Infiltration Dynamics in Thermal Barrier Coatings
复制标题
DOI：
10.2514/1.t6171
复制
发表时间：
2021-02
影响因子：
2.1
通讯作者：
Timothy W. Munuhe;Liang Zhu;Ronghui Ma
中科院分区：
文献类型：
--
作者：
Timothy W. Munuhe;Liang Zhu;Ronghui Ma
熔融钙镁铝硅酸盐 (CMAS) 渗透到燃气轮机的热障涂层 (TBC) 中会导致陶瓷面涂层丧失应变耐受性和分层。为开发...
Molten calcium–magnesium–alumino–silicate (CMAS) infiltration into thermal barrier coatings (TBCs) of gas turbines causes loss of strain tolerance and delamination of the ceramic topcoat. To develo...