Fabrication of thin Ni3Al foils by cold rolling
Fabrication of thin Ni3Al foils by cold rolling
复制标题
冷轧制备薄 Ni3Al 箔
DOI：
10.1016/s1359-6462(02)00139-2
复制
发表时间：
2002
影响因子：
6
通讯作者：
T. Hirano
中科院分区：
文献类型：
--
作者：
M. Demura;K. Kishida;Y. Suga;Motohiro Takanashi;T. Hirano
采用冷轧法制备了厚度为23 μm、宽度为50 mm的单晶Ni3Al薄膜。研究了铝箔的轧制织构和基本力学性能。滚动纹理由（101）[121 ā]和（101）[1 ā 21]两部分组成。该箔具有较高的拉伸断裂强度，无塑性伸长。然而，它们的弯曲延展性是相当显著的。
Cold rolling of single-crystalline Ni3Al was performed to fabricate thin foils of 23 μm in thickness and 50 mm in width. The rolling texture and basic mechanical properties of the foils were examined. The rolling texture consisted of two components, (101)[121 ̄ ] and (101)[1 ̄ 21]. The foils exhibited high tensile fracture strength without plastic elongations. However, their bending ductility was quite remarkable.