IrO2 coated TiO2 core-shell microparticles advance performance of low loading proton exchange membrane water electrolyzers
IrO2 coated TiO2 core-shell microparticles advance performance of low loading proton exchange membrane water electrolyzers
复制标题
DOI：
10.1016/j.apcatb.2020.118762
复制
发表时间：
2020-07-15
影响因子：
22.1
通讯作者：
Thiele, Simon
中科院分区：
文献类型：
--
作者：
Van Pham, Chuyen;Buehler, Melanie;Thiele, Simon
Herein we present novel IrO2 coated TiO2 core-shell microparticles (IrO2@TiO2) as an oxygen evolution reaction catalyst. We compare the IrO2@TiO2 catalyst to commercial TiO2 supported IrO2 catalyst (IrO2/TiO2) and pure IrO2 catalyst powder. A stability analysis via on-line inductively coupled plasma mass spectrometry based on the S-number, a descriptor considering both energy efficiency and catalyst utilization efficiency, shows that the IrO2@TiO2 catalyst shows high potential for practical applications. This was further confirmed by full-cell tests showing superior performance of the IrO2@TiO2 catalyst with moderate and low loadings of 1.2 mg(Ir) cm(-2) and 0.4 mg(Ir) cm(-2), respectively. The core-shell catalyst is synthesized via facile route suitable for large quantifies. Moreover, stable inks from the synthesized catalyst powder make this system appealing for large scale manufacturing of cells. Given the facile synthesis route, high activity, and good stability, the IrO2@TiO2 catalyst is potentially suitable for industry proton exchange membrane water electrolysis application.