Plasmon enhanced polymer solar cells by spin-coating Au nanoparticles on indium-tin-oxide substrate
Plasmon enhanced polymer solar cells by spin-coating Au nanoparticles on indium-tin-oxide substrate
复制标题
通过在氧化铟锡基底上旋涂金纳米粒子来增强等离子激元聚合物太阳能电池
DOI：
10.1063/1.4754839
复制
发表时间：
2012-09
影响因子：
4
通讯作者：
Liu, X.
中科院分区：
文献类型：
--
作者：
Gao, H. L.;Zhang, X. W.;Yin, Z. G.;Tan, H. R.;Zhang, S. G.;Meng, J. H.;Liu, X.
为了增强聚合物太阳能电池的光吸收，在沉积缓冲层之前，通过在氧化铟锡基板上旋涂金胶体溶液，将不同尺寸的金纳米颗粒（NP）掺入到器件中。研究发现，加入60nm Au NPs后，本体异质结电池的功率转换效率可以从3.50%提高到4.07%，相当于提高了16%。器件性能的提高归因于金纳米粒子的局域表面等离子体激发。我们在此报告的方法是一种简单且快速的解决过程。
To enhance light absorption in polymer solar cells, the Au nanoparticles (NPs) with different sizes were incorporated to the devices by spin-coating Au colloid solution on the indium-tin-oxide substrates prior to deposition of buffer layer. It has been found that the power conversion efficiency of bulk heterojunction cells can be increased from 3.50% to 4.07% after incorporating the 60 nm Au NPs, corresponding to an improvement of 16%. The improved device performance is ascribed to the localized surface plasmon excitation of the Au NPs. The method we report herein is a kind of simple and quick solution process.
登录
查看更多内容
影响因子：
4
作者：
Akimov, Yu A.;Koh, W. S.;Ren, S.
通讯作者：
Ren, S.
影响因子：
17.1
作者：
Kim, Chul-Hyun;Cha, Sang-Ho;Jin, Sung-Ho
通讯作者：
Jin, Sung-Ho
影响因子：
4
作者：
Fengxian Xie;W. Choy;Charlie C. D. Wang;W. Sha;D. Fung
通讯作者：
Fengxian Xie;W. Choy;Charlie C. D. Wang;W. Sha;D. Fung
影响因子：
27.8
作者：
Wang, Dong Hwan;Park, Keum Hwan;Heeger, Alan J.
通讯作者：
Heeger, Alan J.
影响因子：
29.4
作者：
Heo, Mihee;Cho, Heesook;Kim, Jin Young
通讯作者：
Kim, Jin Young