Effect of aging on martensitic transformation behavior of Ti48.8Ni50.8V0.4 alloy
Effect of aging on martensitic transformation behavior of Ti48.8Ni50.8V0.4 alloy
复制标题
时效对Ti48.8Ni50.8V0.4合金马氏体相变行为的影响
DOI：
10.1007/s10853-011-5593-6
复制
发表时间：
2011-05
影响因子：
4.5
通讯作者：
C. Y. Chung
中科院分区：
文献类型：
--
作者：
Y. X. Tong;C. Q. Liang;F. Chen;L. Li;Y. F. Zheng;C. Y. Chung
研究了时效对Ti48.8Ni50.8V0.4合金马氏体相变的影响。结果表明，固溶处理后的形状记忆合金的马氏体相变为典型的单阶段相变过程。在不同温度下时效0.5h的样品的相变温度均低于固溶处理的合金。随着时效温度的升高，相变温度升高。在500 °C下老化后，样品表现出多阶段转变。在500 ℃时效5 h以上的试样，冷却时发生A → R→M1和A → M2的相变，加热时发生M2 → A和M1 → A的相变。
In this article, the effect of aging on martensitic transformation of Ti48.8Ni50.8V0.4 alloy was investigated. The results show that the martensitic transformation of the solution-treated shape memory alloy is a typical single-stage transformation process. The transformation temperatures of the samples aged at different temperatures for 0.5 h were lower as compared to that of the solution-treated alloy. With the increase of aging temperature, the transformation temperatures increase. After aging at 500 °C, the samples exhibit a multiple-stage transformation. The samples after aging at 500 °C for more than 5 h resulted in the transformation sequence of A → R→M1 and A → M2 upon cooling and M2 → A and M1 → A upon heating.
登录
查看更多内容
DOI：
10.1016/0956-7151(90)90137-6
发表时间：
1990-01-01
期刊：
ACTA METALLURGICA ET MATERIALIA
影响因子：
--
作者：
WU, SK;LIN, HC;CHOU, TS
通讯作者：
CHOU, TS
DOI：
10.1016/0956-716x(93)90031-m
发表时间：
1993-03
期刊：
Scripta Metallurgica Et Materialia
影响因子：
--
作者：
D. Favier;Yinong Liu;P. McCormick
通讯作者：
D. Favier;Yinong Liu;P. McCormick
影响因子：
4.4
作者：
Chen, F.;Tong, Y. X.;Liu, Y.
通讯作者：
Liu, Y.
影响因子：
9.4
作者：
H. Rösner;P. Schlossmacher;A. Shelyakov;A. Glezer
通讯作者：
H. Rösner;P. Schlossmacher;A. Shelyakov;A. Glezer
DOI：
10.1016/0001-6160(88)90037-5
发表时间：
1988
期刊：
Acta Metallurgica
影响因子：
--
作者：
S. Miyazaki;C. M. Wayman
通讯作者：
S. Miyazaki;C. M. Wayman