Glass/nylon-6.6 composites: Delamination resistance testing
Glass/nylon-6.6 composites: Delamination resistance testing
复制标题
玻璃/尼龙 6.6 复合材料：抗分层测试
DOI：
10.1016/0266-3538(90)90059-e
复制
发表时间：
1990
影响因子：
9.1
通讯作者：
D. R. Moore
中科院分区：
文献类型：
--
作者：
P. Davies;D. R. Moore
本文描述了一系列单向连续玻璃纤维增强尼龙66复合材料的分层试验。首先，从“循环赛”的欧洲骨折组的聚合物和复合材料工作组进行的演习的结果进行了说明。在这项工作中出现了一些问题，随后的工作，以解决这些困难，并解释在这种材料中的分层的机制，模式I和模式II加载下，然后提出。
This paper describes a series of delamination tests on unidirectional continuous glass-fibre-reinforced Nylon-66 composites. Firstly the results from a ‘round-robin’ exercise carried out by the Polymers and Composites Task Group of the European Group on Fracture are described. A number of problems arose during this exercise, and subsequent work to resolve these difficulties and to explain the mechanisms of delamination in this material, under mode I and mode II loading, is then presented.