Residual Stress, Thermomechanics & Infrared Imaging, Hybrid Techniques and Inverse Problems, Volume 8
Residual Stress, Thermomechanics & Infrared Imaging, Hybrid Techniques and Inverse Problems, Volume 8
复制标题
残余应力，热力学
DOI：
10.1007/978-3-319-00876-9_5
复制
发表时间：
2014
期刊：
影响因子：
--
通讯作者：
Tomlinson R
中科院分区：
文献类型：
--
作者：
Tomlinson R
The behaviour of crack growth in fibre metal laminates (FML) was investigated using Thermoelastic Stress Analysis (TSA). Fatigue tests were performed on Single Edge Notch Tension (SENT) specimens and thermoelastic data recorded. A Newton–Raphson iteration combined with a least-squares approach was used to fit equations describing the stress field around the fatigue crack tip to the thermoelastic data. The stress intensity factor range was thus determined at intervals of fatigue crack growth. By correlating the experimental results with a phenomenological crack growth prediction model, it was shown that our thermoelastic methodology which had been used previously for crack studies in monolithic metal specimens is capable of determining accurately fracture parameters in hybrid materials. The thermoelastic technique also allows identification of the crack tip in the metal layer, thus fatigue crack growth rate was determined easily. The experimental results agreed with the general trend reported elsewhere, of decreasing crack growth rate in FMLs. Delamination between the metal and fibre layers in the crack wake was investigated by comparing thermoelastic data with ultrasound measurements. It was found that the out-of-phase thermoelastic signal gave an accurate representation of the delamination in the crack wake. TSA, therefore, shows great potential for several aspects of fracture study in FMLs.
登录
查看更多内容
轮胎-轮辋界面处的胎圈接触压力测量
影响因子：
2.2
作者：
J. D. Walter;R. K. Kiminecz
通讯作者：
R. K. Kiminecz
影响因子：
6
作者：
N. Tseng;R. Pelle;J. Chang
通讯作者：
J. Chang
飞机车轮轮胎-车轮界面载荷的测定
影响因子：
2.2
作者：
S. Kandarpa;B. Spencer;D. Kirkner;M. Champion
通讯作者：
M. Champion
影响因子：
2.2
作者：
J. Sherwood;B. K. Fussell;W. R. Edwards;T. Gross;D. Watt
通讯作者：
D. Watt
使用热成像方法对 C36000 铜合金进行疲劳表征
影响因子：
2.2
作者：
L. Rego;J. Castro;J. Freire;V. Paiva
通讯作者：
V. Paiva