Stress Corrosion Cracking Behavior of Hardening-Treated 13Cr Stainless Steel

Stress Corrosion Cracking Behavior of Hardening-Treated 13Cr Stainless Steel
复制标题

硬化处理13Cr不锈钢的应力腐蚀开裂行为

DOI：
10.1088/1757-899x/317/1/012073
复制
发表时间：
2018
期刊：
IOP Conference Series: Materials Science and Engineering
影响因子：
--
通讯作者：
Sakai Yoshihiro
Sakai Yoshihiro
中科院分区：
--
文献类型：
--
作者：
Niu Li-Bin;Ishitake Hisamitsu;Izumi Sakae;Shiokawa Kunio;Yamashita Mitsuo;Sakai Yoshihiro

文献摘要

相似文献

通过SSRT试验和恒载试验，研究了13Cr不锈钢硬化处理后材料的应力腐蚀开裂行为。在模拟地热水中，甚至在没有添加杂质的试验水中，硬化处理后的材料由于敏化而表现出脆性沿晶断裂，这是由目前的硬化处理引起的。
Stress corrosion cracking (SCC) behavior of the hardening-treated materials of 13Cr stainless steel was examined with SSRT tests and constant load tests. In the simulated geothermal water and even in the test water without addition of impurities, the hardening-treated materials showed a brittle intergranular fracture due to the sensitization, which was caused by the present hardening-treatments.