Effect of γ precipitates on martensitic transformation and magnetic properties in aged Mn–Ni–Ga alloys
Effect of γ precipitates on martensitic transformation and magnetic properties in aged Mn–Ni–Ga alloys
复制标题
γ析出相对时效Mn-Ni-Ga合金马氏体相变和磁性能的影响
DOI：
10.1063/1.2943661
复制
发表时间：
2008-06
影响因子：
4
通讯作者：
中科院分区：
文献类型：
--
作者：
时效Mn50Ni25Ga25合金的差示扫描量热曲线观察到多个马氏体相变峰，相变温度随时效温度的变化而变化。在磁转变温度以上时效，磁性和矫顽力均得到增强。在873K时效时，合金的最大磁化强度可达54emu∕g，两相之间的磁化差为28emu∕g。而573K时效合金的矫顽力高达1.2kOe，具有较高的饱和场，这可以从畴壁钉钉的角度来理解。
Multiple martensitic transformation peaks were observed from differential scanning calorimetry curves in aged Mn50Ni25Ga25 alloys in which transformation temperature varied with aging temperature. The magnetization and coercivity were enhanced as a result of aging above magnetic transition temperature. A maximum magnetization up to 54emu∕g and a magnetization difference between two phases of 28emu∕g was achieved in the alloy aged at 873K. However, coercivity as large as 1.2kOe was obtained in 573K aged alloy, with a high saturation field, which can be understood in terms of domain wall pinning.
登录
查看更多内容
影响因子：
64.8
作者：
Kainuma, R;Imano, Y;Ishida, K
通讯作者：
Ishida, K
DOI：
10.1088/0953-8984/15/22/317
发表时间：
2003-05
期刊：
Journal of Physics: Condensed Matter
影响因子：
--
作者：
M. Kreissl;K. Neumann;T. Stephens;K. Ziebeck
通讯作者：
M. Kreissl;K. Neumann;T. Stephens;K. Ziebeck
影响因子：
4
作者：
Oikawa, K;Ota, T;Ishida, K
通讯作者：
Ishida, K
NiCoMnGa合金中磁场诱导可逆马氏体相变的实现
影响因子：
4
作者：
通讯作者：
--
影响因子：
3.2
作者：
G. Prokop;W. Soffa
通讯作者：
G. Prokop;W. Soffa