Effect of organically modified sepiolite as inorganic nanofiller on the anti-corrosion resistance of epoxy coating
Effect of organically modified sepiolite as inorganic nanofiller on the anti-corrosion resistance of epoxy coating
复制标题
有机改性海泡石作为无机纳米填料对环氧涂料防腐性能的影响
DOI：
10.1016/j.matlet.2019.126941
复制
发表时间：
2020-02
影响因子：
3
通讯作者：
Ouyang Xiaoping
中科院分区：
文献类型：
--
作者：
Xiong Hailong;Qi Fugang;Zhao Nie;Yuan Heng;Wan Pengying;Liao Bin;Ouyang Xiaoping
本文报道了一种新型无机纳米填料海泡石（SEP），它是通过酸和偶联剂KH 570改性的。然后将不同含量的有机改性海泡石（OMSEP）纤维加入到环氧树脂（EP）基体中。结果表明，OMSEP的加入显著提高了EP涂层的耐蚀性。当OMSEP的质量分数为3%时，EP涂层的耐蚀性最好。浸渍72 h的3wt%OMSEP涂层的低频阻抗比浸渍6 h的EP涂层高3个数量级。
We report a new inorganic nanofiller sepiolite (SEP), which is modified by acid and coupling agent KH570. The different content of organically modified sepiolite (OMSEP) fibers are then added into the epoxy resin (EP) matrix. The results reveal the corrosion resistance of EP coating improved significantly with the addition of OMSEP. When containing 3 wt% OMSEP, the EP coating has the best corrosion resistance. The impedance at low frequencies of the 3 wt% OMSEP coating immersed for 72 h is three orders of magnitude higher than the 6-hour EP coating.
登录
查看更多内容
影响因子：
5.2
作者：
Guanzheng Zhuang;Zepeng Zhang;Huiwen Chen
通讯作者：
Guanzheng Zhuang;Zepeng Zhang;Huiwen Chen
影响因子：
6.6
作者：
Kongparakul, Suwadee;Kornprasert, Saktip;Guan, Guoqing
通讯作者：
Guan, Guoqing
影响因子：
9.5
作者：
Ruixia Yuan;Shiqi Wu;Peng Yu;Baohui Wang;Liwen Mu;Xiguang Zhang;Yixing Zhu;Bin Wang;Huaiyuan Wang
通讯作者：
Ruixia Yuan;Shiqi Wu;Peng Yu;Baohui Wang;Liwen Mu;Xiguang Zhang;Yixing Zhu;Bin Wang;Huaiyuan Wang
商业高颜料环氧涂料在海洋交变静水压力下的失效行为
影响因子：
6.6
作者：
Tian, Wenliang;Meng, Fandi;Wang, Fuhui
通讯作者：
Wang, Fuhui
影响因子：
5.6
作者：
Di Credico, Barbara;Cobani, Elkid;Morazzoni, Franca
通讯作者：
Morazzoni, Franca