High-temperature dielectric relaxation mechanism in Ba4SmFe0.5Nb9.5O30 tungsten bronze ceramics
High-temperature dielectric relaxation mechanism in Ba4SmFe0.5Nb9.5O30 tungsten bronze ceramics
复制标题
Ba4SmFe0.5Nb9.5O30钨青铜陶瓷的高温介电弛豫机制
DOI：
10.1016/j.ceramint.2018.08.109
复制
发表时间：
2018-11
影响因子：
5.2
通讯作者：
Fang Liang
中科院分区：
文献类型：
--
作者：
Hu Changzheng;Guo Zhe;Wu Shan;Sun Zhen;Li Chunchun;Liu Laijun;Fang Liang
研究了未填充钨青铜陶瓷Ba_4SmFe_（0.5）Nb_（9.5）O_（30）的高温烧结性能。温度介电性能和变温XRD数据以及XPS数据表明，BSFN陶瓷在25 °C至450 °C之间没有相变;在350 °C附近的高温弛豫行为与氧缺陷密切相关。Ba_4SmFe_（0.5）Nb_（9.5）O_（30）陶瓷电导弛豫的频率依赖关系符合Arrhenius方程，Ea~ 0.65 eV。
The high temperature dielectrics properties of unfilled tungsten bronze ceramics, Ba4SmFe0.5Nb9.5O30, were studied. The temperature dielectric properties and the variable temperature XRD data, in addition to the XPS data indicated that BSFN ceramics have no phase changes from 25 °C to 450 °C; the high temperature relaxation behaviour around 350 °C is closely related to the oxygen defects. Frequency dependence of temperature electrical conductivity relaxation of Ba4SmFe0.5Nb9.5O30ceramics was well fitted by the Arrhenius relationship with Ea~ 0.65 eV.
登录
查看更多内容
新型Ba4SmFe0.5Nb9.5O30钨青铜陶瓷的弛豫行为和铁电性能
影响因子：
5.2
作者：
Changzheng Hu;Zhen Sun;Qihua Zhu;Fengqi Lu;Chunchun Li;Laijun Liu;Liang Fang
通讯作者：
Liang Fang
影响因子：
6.7
作者：
Yamashita, Toru;Hayes, Peter
通讯作者：
Hayes, Peter
影响因子：
2.1
作者：
B. Kang;Si-Kyung Choi
通讯作者：
B. Kang;Si-Kyung Choi
影响因子：
3.7
作者：
Ang, C;Yu, Z;Cross, LE
通讯作者：
Cross, LE
影响因子：
3.7
作者：
A. Rotaru;D. Arnold;A. Daoud-Aladine;F. Morrison
通讯作者：
A. Rotaru;D. Arnold;A. Daoud-Aladine;F. Morrison