Galvanic Corrosion of Brass /steel 907A Couple in Artificial Seawater
Galvanic Corrosion of Brass /steel 907A Couple in Artificial Seawater
复制标题
人工海水中黄铜/钢 907A 的电偶腐蚀
DOI：
10.20964/110437
复制
发表时间：
2016-05
影响因子：
1.5
通讯作者：
Chunan Cao
中科院分区：
文献类型：
--
作者：
Li Jiang;Qingsong Yang;Xiaoqing Du;Zhen Xu;Yu Chen;Zhao Zhang;Jianqing Zhang;Chunan Cao
采用电化学阻抗谱和电化学噪声技术研究了不同阴阳极面积比的黄铜/907 A钢电偶腐蚀行为。实验结果表明，电偶腐蚀在初始24 h内加速，随后（26 h ~ 720 h）逐渐减弱。用能量分布图（EDP）表征了产物的成核、生长和成膜过程，并采用两个参数（n1和n2）区分成核和生长过程。根据n1和n2的变化趋势，将电偶腐蚀过程分为波动阶段和稳定阶段。随着阴/阳极面积比的增大，黄铜/907 A钢电偶的腐蚀速率增大，波动阶段的时间延长。
Galvanic corrosion of brass /steel 907A couples with various cathode /anode area ratios were examined by electrochemical impedance spectroscopy and electrochemical noise technique. Experimental results show that the galvanic corrosion of couples accelerate within the initial 24h, and then decrease in the later time (from 26h to 720h). The products nucleation, growth, film formation stages are characterized using energy distribution plots (EDP) and two parameters (n1 and n2) are adopted to differentiate the nucleation and growth processes. According to the variation tendency of n1 and n2, galvanic corrosion process are divided into fluctuating stage and stabilization stage. As the cathode /anode area ratios increase, the corrosion rates of brass /steel 907A couples increase and the period of fluctuating stage lengthens.
登录
查看更多内容
影响因子：
3.9
作者：
K. Lichti;M. Ko;L. Wallis
通讯作者：
K. Lichti;M. Ko;L. Wallis
氟硼酸亚锡酸浴中锡在双还原钢基体上的电化学成核和生长
影响因子：
4.5
作者：
Huang, Xianqiu;Chen, Yu;Zhang, Jianqing
通讯作者：
Zhang, Jianqing
影响因子：
3.3
作者：
Sunil Kumar Thamida
通讯作者：
Sunil Kumar Thamida
影响因子：
7.8
作者：
A. Khadom;Ahmed Hassan;Baker M. Abod
通讯作者：
A. Khadom;Ahmed Hassan;Baker M. Abod
影响因子：
1.2
作者：
R. Moshrefi;M. G. Mahjani;A. Ehsani;M. Jafarian
通讯作者：
R. Moshrefi;M. G. Mahjani;A. Ehsani;M. Jafarian