On the Formation Mechanism of the V Segregation in Steel Ingot
On the Formation Mechanism of the V Segregation in Steel Ingot
复制标题
钢锭V偏析形成机理的探讨
DOI：
10.2355/isijinternational1966.14.296
复制
发表时间：
1974
影响因子：
1.8
通讯作者：
Takehiro Miyamoto
中科院分区：
文献类型：
--
作者：
Koreaki Suzuki;Takehiro Miyamoto
根据对种族隔离形成的研究，它似乎受到以下三个因素的影响；(3)热层法、重力层法和树突mOlJ法。在顺序10中，显示了当每个因子单独变化或相互变化时，Ii隔离将如何受到影响。对砂型钢锭进行了一些调查。根据所得结果，讨论了基于V偏析的形成机理，并对实验结果进行了较好的解释
Synopsis According 10 lhe sludies on lhe formalion of lhe Ii segregalion, i l seems 10 be affecled b), lhe following lhree faclors; lhe lhermal slale , lhe gravilalional aclion , and lhe dendrile mOlJ)lwlogy. In order 10 show how lhe Ii segregalion would be influenced when each faclor was varied indel)endenlly or mulual!.>" some invesligalions have been made on sand-casl ingots . A discussion was made 011 lhe formalion mechanism of lhe V segregation based ul)on the obtained results alld tlze experimental results were well explained b), the llzemy of suclion due to the volume shrinkage of mollen