A glass coating prepared by pulse arc discharge deposition for oxidation protection of carbon/carbon composites
A glass coating prepared by pulse arc discharge deposition for oxidation protection of carbon/carbon composites
复制标题
脉冲电弧放电沉积制备的碳/碳复合材料氧化防护玻璃涂层
DOI：
10.1016/j.apsusc.2014.08.013
复制
发表时间：
2014-02
影响因子：
6.7
通讯作者：
Huang Jianfeng
中科院分区：
文献类型：
--
作者：
Zhang Yongliang;Huang Jianfeng
采用脉冲电弧放电沉积(PADD)技术制备了碳化硅预涂覆碳/碳复合材料(SiC-C/C)氧化防护玻璃涂层。研究了玻璃/碳化硅涂层的物相组成、微观结构和抗氧化性能。结果表明，脉冲电弧放电沉积是获得致密无裂纹涂层的有效途径，这是由于脉冲技术与电弧放电烧结工艺相结合的低温条件所致。玻璃/碳化硅多层膜能有效地保护C/C复合材料在1773℃、292 h的空气中氧化，失重率为2.04%。
Pulse arc discharge deposition (PADD) was developed to prepare an oxidation protective borosilicate glass coating for SiC pre-coated carbon/carbon composites (SiC–C/C). The phase compositions, microstructure and oxidation resistance of the as-prepared glass/SiC coating were investigated. The results show that pulse arc discharge deposition is an effective route to achieve a dense and crack-free outer coating, which is attributed to a low temperature with pulse technique and arc discharge sintering process combined. The glass/SiC multilayer coating can effectively protect C/C composites from oxidation in air at 1773 K for 292 h with a weight loss of 2.04%.
登录
查看更多内容
影响因子：
8.3
作者：
Yulei Zhang;Wen-Ying Zeng;Hejun Li;Kezhi Li
通讯作者：
Yulei Zhang;Wen-Ying Zeng;Hejun Li;Kezhi Li
影响因子：
10.9
作者：
Li, Ke-zhi;Jing, Xie;Guo Ling-jun
通讯作者：
Guo Ling-jun
影响因子：
8.3
作者：
Wang Yalei;X. Xiong;Guo-dong Li;Huaifei Liu;Z. Chen;Wei Sun;Xue-jia Zhao
通讯作者：
Wang Yalei;X. Xiong;Guo-dong Li;Huaifei Liu;Z. Chen;Wei Sun;Xue-jia Zhao
影响因子：
3.9
作者：
J. W. Hinze;H. C. Graham
通讯作者：
J. W. Hinze;H. C. Graham
影响因子：
5.7
作者：
T. Damjanović;C. Argirusis;B. Jokanović;G. Borchardt;K. Moritz;E. Müller;R. Herbig;R. Weiss
通讯作者：
T. Damjanović;C. Argirusis;B. Jokanović;G. Borchardt;K. Moritz;E. Müller;R. Herbig;R. Weiss