Microstructural characteristics and mechanical properties of IC10 superalloy and (CoCrNi)94Al3Ti3 MEA joint brazed using NiCrSiB filler
Microstructural characteristics and mechanical properties of IC10 superalloy and (CoCrNi)94Al3Ti3 MEA joint brazed using NiCrSiB filler
复制标题
DOI：
10.1016/j.matchar.2022.111964
复制
发表时间：
2022
期刊：
影响因子：
--
通讯作者：
Jinglong Li
中科院分区：
文献类型：
--
作者：
Shiwei Li;Yu Peng;Yajie Du;Lin Yuan;Jiangtao Xiong;Jinglong Li
This study focuses on the brazing of IC10 Ni 3 Al-based superalloy to (CoCrNi) 94 Al 3 Ti 3 medium-entropy alloy (MEA) using a NiCrSiB filler metal. The microstructure of the brazed joint was comprehensively investigated, and the forming mechanism of the joint was elucidated. The mechanical properties and fracture behavior of the joint were evaluated. The diffusion of boron from the filler to substrates led to the diffusion-affected zone (DAZ), and the M 3 B 2 - and M 5 B 3 -type boride were precipitated with the coherence of (3 1 0) BCT //(2 0 0) FCC (M 3 B 2 ) and (0 0 2) BCT //(2 0 0) FCC (M 5 B 3 ) adjacent to the IC10 and MEA substrate, namely the DAZ I and II respectively. In addition, the edge dislocation reduced the mismatch between the M 3 B 2 boride and the γ matrix. The isothermal solidification zone (ISZ) was formed near the DAZ when the liquidus temperature reached the brazing temperature due to the diffusion of boron and Si and the dissolution of substrates. The formation of ISZ was effectively activated at high brazing temperatures (1090, 1120, and 1150 °C). The athermal solidification zone (ASZ) was detected in the joint brazed at adopted temperatures, which mainly dominated by eutectic reactions and driven by cooling. The ASZ decreased shear strength of the defect-free joint, and readily accelerated initiation and propagation of cracks. The maximum shear strength of 554 MPa was obtained when the joint was brazed at 1120 °C for 10 min. The fracture mainly occurred in the ASZ (semi-cleavage), and passing through the DAZ (semi-cleavage) and ISZ (dimples). • The brazing of IC10 and (CoCrNi) 94 Al 3 Ti 3 MEA was achieved using a NiCrSiB filler. • The M 3 B 2 - and M 5 B 3 -type borides in the DAZ exhibited coherent with the matrix. • The microstructural evolution and mechanical properties were evaluated. • .