Structural and electrochemical properties of LiV3O8 prepared by combustion synthesis
Structural and electrochemical properties of LiV3O8 prepared by combustion synthesis
复制标题
燃烧合成LiV3O8的结构和电化学性能
DOI：
10.1016/j.jallcom.2009.06.188
复制
发表时间：
2009-11
影响因子：
6.2
通讯作者：
Yuan, Hua-Tang
中科院分区：
文献类型：
--
作者：
Jiao, Li-Fang;Si, Yu-Chang;Wang, Yong-Mei;Li, Hai-Xia;Yuan, Hua-Tang
以金属硝酸盐为氧化剂，尿素为燃料，采用燃烧合成法制备了LiV 3 O 8粉体。讨论了（Li+V）/CO（NH 2）2配比和热处理温度对材料结构和电化学性能的影响。电化学性能测试结果表明，在300°C、（Li+V）/CO（NH 2）2比为1：0.5的条件下合成的样品B1具有最高的首次放电容量（317.3mAhg− 1）和最好的循环性能（30次循环后为238.9mAhg− 1）。
LiV3O8powders were prepared by combustion synthesis, using metallic nitrates as the oxidant and metal sources and urea as fuel. The effect of (Li+V)/CO(NH2)2ratio and heat-treatment temperature on the structure and electrochemical properties were discussed. The electrochemical behavior of the product showed that sample B1synthesized at 300°C with 1:0.5 ratio of (Li+V)/CO(NH2)2showed the highest initial discharge capacity of 317.3mAhg−1and the best cycle ability with 238.9mAhg−1after 30 cycles.
登录
查看更多内容
影响因子：
9.2
作者：
G. Pistola;M. Pasquali;M. Tocci;V. Manev;R. Moshtev
通讯作者：
G. Pistola;M. Pasquali;M. Tocci;V. Manev;R. Moshtev
DOI：
10.1016/s0921-5093(99)00715-7
发表时间：
2000-04
影响因子：
6.4
作者：
Seunghoon Lee;Jong-Hyun Lee;Yong-Ho Lee;D. Shin;Yong-Seog Kim
通讯作者：
Seunghoon Lee;Jong-Hyun Lee;Yong-Ho Lee;D. Shin;Yong-Seog Kim
影响因子：
3.2
作者：
G. Pistoia;S. Panero;M. Tocci;R. Moshtev;V. Manev
通讯作者：
G. Pistoia;S. Panero;M. Tocci;R. Moshtev;V. Manev
影响因子：
3
作者：
Jinggang Xie;Jin-Xi Li;Hui Zhan;Yunhong Zhou
通讯作者：
Jinggang Xie;Jin-Xi Li;Hui Zhan;Yunhong Zhou
影响因子：
6.2
作者：
Junli Sun;Lifang Jiao;H. Yuan;Li Liu;Xin Wei;Yanli Miao;Lin Yang;Yong-mei Wang
通讯作者：
Junli Sun;Lifang Jiao;H. Yuan;Li Liu;Xin Wei;Yanli Miao;Lin Yang;Yong-mei Wang