Grain refining potency of Al-B master alloy on pure aluminum
Grain refining potency of Al-B master alloy on pure aluminum
复制标题
Al-B中间合金对纯铝的晶粒细化效果
DOI：
10.1016/j.scriptamat.2011.03.001
复制
发表时间：
2011-06
影响因子：
6
通讯作者：
Li T.
中科院分区：
文献类型：
--
作者：
Wang T.;Chen Z.;Fu H.;Xu J.;Fu Y.;Li T.
确定了Al-B中间合金是纯铝的有效晶粒细化剂。在不进行任何搅拌的情况下，通过卤化盐途径，通过改变盐的加入温度750、850和950℃制备了3种Al-3B中间合金。它们在纯铝上均表现出细化晶粒的能力，其中在950℃的加入温度下效果最好。在接种后的保温过程中也注意到这种母合金的抗褪色性。
Al–B master alloys were ascertained to be efficient grain refiners on pure aluminum. Without introducing any stirring during reaction, three experimental Al–3B master alloys were prepared via the halide salt route by varying the salt addition temperature, i.e. 750, 850 and 950 °C. All of them showed grain refining potency on pure aluminum and that with the 950 °C addition temperature was found to be the most efficient. Resistance to fading was also noted during holding after inoculation with this master alloy.
登录
查看更多内容
DOI：
10.4028/www.scientific.net/msf.217-222.247
发表时间：
1996-05
期刊：
Materials Science Forum
影响因子：
--
作者：
A. Hardmann;F. Hayes
通讯作者：
A. Hardmann;F. Hayes
影响因子：
6.2
作者：
Y. Birol
通讯作者：
Y. Birol
DOI：
10.1016/j.msea.2006.10.145
发表时间：
2007-04
影响因子：
6.4
作者：
S. Nafisi;R. Ghomashchi
通讯作者：
S. Nafisi;R. Ghomashchi
DOI：
10.1007/bf02663335
发表时间：
1971-02
期刊：
Metallurgical Transactions
影响因子：
--
作者：
J. Antonio;L. Lfo
通讯作者：
J. Antonio;L. Lfo
DOI：
10.1007/bf02654921
发表时间：
1976-01-01
期刊：
METALLURGICAL TRANSACTIONS B-PROCESS METALLURGY
影响因子：
--
作者：
JONES, GP;PEARSON, J
通讯作者：
PEARSON, J