Magnetic Properties of Pr-Fe-Co-Nb-B System Exchange Spring Magnets
Magnetic Properties of Pr-Fe-Co-Nb-B System Exchange Spring Magnets
复制标题
Pr-Fe-Co-Nb-B系交换弹簧磁体的磁性能
DOI：
10.1541/ieejfms1990.121.8_784
复制
发表时间：
1998
影响因子：
--
通讯作者：
T. Konishi
中科院分区：
文献类型：
--
作者：
H. Yamamoto;T. Konishi
采用单辊快淬法制备了Pr-Fe-Co-W-B系合金的快淬带。研究了成分、轮速和热处理对磁体性能的影响。对以15.0m/S速度制备的Pr9Fe76.7Co8W0.3B6薄带进行了晶化处理，确定了最佳的热处理条件为600℃，3min，此时(BH)max为148.5 kJ/m3。非晶态Pr9Fe76.7Co8W0.3B6合金的晶化温度系数分别为α(Jr)=-0.03%/℃(可逆)和α(Hcj)=-0.45%/℃(不可逆)。采用600℃热处理3min制备的压型Pr9Fe76.7Co8W0.3B6各向同性粘结磁体的(BH)max为86.00kJ/m3，密度为6.16 mg/m3。
The melt-spun ribbons of Pr-Fe-Co-W-B system alloys were prepared by single roller rapid-quenching method. The effects of composition ， wheel velocity and heat-treatment on the magnetic properties were investigated. The Pr 9 Fe 76.7 Co 8 W 0.3 B 6 ribbon prepared at a wheel velocity of 15.0 m/s were crystallized by heat-treatment ， and the optimum heat-treatment condition was found to be at 600 ℃ for 3 min ， then the value of (BH) max was 148.5 kJ/m 3 . The temperature coefficients of J r and H cJ for the ribbons crystallized from the amorphous Pr 9 Fe 76.7 Co 8 W 0.3 B 6 alloy were α (J r )= － 0.03 %/ ℃ (reversible)and α (H cJ )= － 0.45 %/ ℃ (irreversible) ， respectively. The value of (BH) max for the compression molding Pr 9 Fe 76.7 Co 8 W 0.3 B 6 isotropic bonded magnet prepared by using the ribbons annealed at 600 ℃ for 3 min is 86.00 kJ/m 3 and the density is 6.16 Mg/m 3 .
Nb和V添加对镨铁钴硼淬火薄带磁性能的影响
DOI：
--
发表时间：
2004
期刊：
電気学会マグネティックス研究会資料, MAG-04-216(11月)
影响因子：
--
作者：
山元洋;古澤鋼
通讯作者：
古澤鋼
Co层间静磁相互作用对Co/Cu/Co三层环结构磁性能的影响
DOI：
--
发表时间：
2009
期刊：
影响因子：
--
作者：
宮脇哲也;渡邉祐介;好田誠;斉藤今朝美;三谷誠司;高梨弘毅;新田淳作
通讯作者：
新田淳作