Crystal Growth and Properties of AlLiB14
Crystal Growth and Properties of AlLiB14
复制标题
DOI：
10.1143/jjap.41.l928
复制
发表时间：
2002-08
影响因子：
1.5
通讯作者：
K. Kudou;S. Okada;T. Mori;K. Iizumi;T. Shishido;Takaho Tanaka;I. Higashi;K. Nakajima;P. Rogl;Y. Andersson;T. Lundström
中科院分区：
文献类型：
--
作者：
K. Kudou;S. Okada;T. Mori;K. Iizumi;T. Shishido;Takaho Tanaka;I. Higashi;K. Nakajima;P. Rogl;Y. Andersson;T. Lundström
以Li_2B_4O_7和无定形硼为原料，在氩气保护下，从高温铝溶液中生长出AlLiB_（14）单晶。得到的AlLiB 14晶体具有良好的（010）或（001）面，并且是具有金属光泽的红黑色。AlLiB_（14）晶体的最大尺寸约为4.6×0.3×0.3 mm ~ 3。测量了晶体的低温磁化率和维氏显微硬度，并研究了晶体在空气中的高温抗氧化性能。
Single crystals of AlLiB14 were grown from a high temperature aluminum solution using Li2B4O7 and amorphous boron as raw materials under an argon atmosphere. The AlLiB14 crystals obtained had well developed (010) or (001) faces, and were reddish black with a metallic luster. The maximum dimensions of AlLiB14 crystals obtained were about 4.6×0.3×0.3 mm3. Magnetic susceptibility at low temperature and Vickers microhardness of the as-grown crystals were measured, and the oxidation resistance in air at high temperatures was studied.