Influence of Carisolv™ for resin adhesion to sound human primary dentin and young permanent dentin
Influence of Carisolv™ for resin adhesion to sound human primary dentin and young permanent dentin
复制标题
DOI：
10.1016/s0300-5712(01)00006-9
复制
发表时间：
2001-03-01
影响因子：
4.4
通讯作者：
Goto, G
中科院分区：
文献类型：
--
作者：
Hosoya, Y;Kawashita, Y;Goto, G
目的：本研究旨在评价Carisolv（TM）（Medi Team）对健康人乳磨牙和年轻恒牙本质树脂粘接的影响。使用两种粘合剂系统和树脂复合材料; SD：Super-Bond D Liner DUAL（R）（Sun Medical）和Clearfil Photo Anterior（R）（Kuraray），以及FB：Imperva Fluorobond（TM）和Lite-FilTM IIA（Shofu）。准备了10组。第1-5组为原始牙本质，第6-10组为永久牙本质。第1组和第6组。应用CarisolvTM并搅拌3分钟，使用SD。第2组和第7组：用10-3溶液（Sun Medical）蚀刻10 s，使用SD。组3和8：用Carisolv（TM）处理，然后蚀刻，使用SD。第4组和第9组：用Carisolv（TM）处理，使用FB。第5组和第10组：使用FB。用扫描电镜观察CarisolvTM、10-3溶液和CarisolvTM +10-3溶液对牙本质微观结构的影响。另外，用扫描电镜观察各组树脂-牙本质界面的微观结构。测试了剪切粘结强度（SBS），并用扫描电镜观察了破坏面。结果：Carisolv对乳牙本质的作用强于恒牙本质。第1-10组的平均SBS（单位：MPa）为：5.6、15.8、7.6、17.5、13.5、8.1、16.2、18.2、31.4和15.5。第9组（Carisolv（TM）处理的恒牙本质）的SBS显著高于其他组。第2、4、5、7、8、10组、第3、5、6组、第1、3、6组之间的SBS无显著差异。意义：酸蚀前Carisolv（R）处理显著降低SD组中的原始牙本质的SBS，但显著增加FB组中的永久牙本质的SBS。(C)2001爱思唯尔科技有限公司版权所有。
Objective: This study evaluated the influence of Carisolv(TM) (Medi Team) for resin adhesion to sound human primary and young permanent dentin.Method: The buccal surfaces of 64 primary molars and 74 premolars were used. Two adhesive systems and resin composites were used; SD: Super-Bond D Liner DUAL(R) (Sun Medical) and Clearfil Photo Anterior(R) (Kuraray), and FB: Imperva Fluorobond(TM) and Lite-Fil(TM) IIA (Shofu). Ten groups were prepared. Groups 1-5 were primary dentin and Groups 6-10 were permanent dentin. Groups 1 and 6. Carisolv(TM) applied and agitated for 3 min, SD was used. Groups 2 and 7: etched with 10-3 solution (Sun Medical) for 10 s, SD was used. Groups 3 and 8: treated with Carisolv(TM) and then etched, SD was used. Groups 4 and 9: treated with Carisolv(TM), FB was used. Groups 5 and 10:FB was used. The microstructural effects of Carisolv(TM), 10-3 solution and Carisolv(TM) plus 10-3 solution applied to dentin were evaluated by SEM. In addition, the microstructure of the resin-dentin interfaces of each group were studied using SEM. Shear bond strengths (SBS) were tested, and the failed surfaces were observed using SEM. Data was statistically analyzed using ANOVA with subsequent application of post hoc Duncan's new multiple range test at p < 0.05.Results: The effect of Carisolv on primary dentin was stronger than that to permanent dentin. The mean SBS (unit:MPa) of Groups 1-10 were: 5.6, 15.8, 7.6, 17.5, 13.5, 8.1, 16.2, 18.2, 31.4 and 15.5. The SBS of Group 9 (Carisolv(TM) treated permanent dentin) was significantly higher than those of other groups. There was no significant difference of SBS among Groups 2, 4, 5, 7, 8 and 10, Groups 3, 5 and 6, and Groups 1, 3 and 6.Significance: Carisolv(R) treatment before etching significantly decreased the SBS to primary dentin in SD groups, but significantly increased the SBS to permanent dentin in FB groups. (C) 2001 Elsevier Science Ltd. All rights reserved.