Synthesis and Electrochemical Properties of Porous Titania Fabricated from Nanosheets
Synthesis and Electrochemical Properties of Porous Titania Fabricated from Nanosheets
复制标题
纳米片多孔二氧化钛的合成及电化学性能
DOI：
10.4028/www.scientific.net/kem.566.111
复制
发表时间：
2013
期刊：
影响因子：
--
通讯作者：
T. Okutani
中科院分区：
文献类型：
--
作者：
M. Sakao;N. Kijima;M. Yoshinaga;J. Akimoto;T. Okutani
以（C4 H9）4 NOH剥离的二氧化钛纳米片为原料，采用喷雾干燥法制备了多孔二氧化钛。氮气吸附-脱附等温线表明，多孔二氧化钛具有由狭缝状孔组成的介孔结构。多孔二氧化钛在液体有机电解质锂电池中充当可再充电活性材料。初始锂嵌入容量为约150 mAh/g（截止电压为1.0 V），其大致对应于Li0.45 TiO 2的组成。
A porous titania was synthesized by spray-drying of titania nanosheets exfoliated by (C4H9)4NOH. Nitrogen adsorption-desorption isotherms showed that the porous titania has a mesoporous structure composed of slit-shaped pores. The porous titania acted as a rechargeable active material in a liquid organic electrolyte lithium cell. An initial lithium insertion capacity was about 150 mAh/g (cut-off voltage of 1.0 V), which approximately correspond to the composition of Li0.45TiO2.
由剥离纳米片制造的薄片二氧化钛的表征和电化学性能
DOI：
--
发表时间：
--
期刊：
Journal of Physics and Chemistry of Solids, (accepted for publication) (掲載確定)
影响因子：
--
作者：
J. Awaka;et al.;Y. Takahashi;N. Kijima
通讯作者：
N. Kijima