Ultra-high temperature oxidation resistance of ZrB2-20SiC coating with TaSi2 addition on siliconized graphite
Ultra-high temperature oxidation resistance of ZrB2-20SiC coating with TaSi2 addition on siliconized graphite
复制标题
硅化石墨上添加TaSi2的ZrB2-20SiC涂层的超高温抗氧化性能
DOI：
10.1016/j.ceramint.2019.05.030
复制
发表时间：
2019-08
影响因子：
5.2
通讯作者：
Meishuan Li
中科院分区：
文献类型：
--
作者：
Yan Ren;Yuhai Qian;Jingjun Xu;Jun Zuo;Meishuan Li
采用料浆法在硅化石墨表面制备了ZrB 2 - 20 SiC和ZrB 2 - 20 SiC-10 TaSi 2（体积分数）涂层。通过感应加热方法将所制备的涂层在1700 °C下在空气中氧化30 min。基于涂层的消耗来评价涂层的抗氧化性。TaSi 2的加入显著提高了ZrB 2 - 20 SiC涂层的抗超高温氧化性能，这是由于在涂层中形成了具有较低透氧性的Ta溶解氧化物层。
ZrB2-20SiC and ZrB2-20SiC-10TaSi2(volume fraction) coatings were prepared on siliconized graphite by slurry method. The as-prepared coatings were oxidized at 1700 °C in air for 30 min by induction heating method. The oxidation resistance of the coatings was evaluated based on the consumption of the coating. The addition of TaSi2significantly improved the ultra-high temperature oxidation resistance of ZrB2-20SiC coating, due to the formation of a Ta dissolved oxide layer with much lower oxygen permeability.
登录
查看更多内容
影响因子：
5.4
作者：
C. Verdon;O. Szwedek;S. Jacques;A. Allemand;Y. Petitcorps
通讯作者：
C. Verdon;O. Szwedek;S. Jacques;A. Allemand;Y. Petitcorps
影响因子：
6
作者：
D. Sciti;Mylène Brach;A. Bellosi
通讯作者：
D. Sciti;Mylène Brach;A. Bellosi
影响因子：
3.9
作者：
B. Warren;A. G. Pincus
通讯作者：
B. Warren;A. G. Pincus
影响因子：
8.3
作者：
M. Dehdashti;W. Fahrenholtz;G. Hilmas
通讯作者：
M. Dehdashti;W. Fahrenholtz;G. Hilmas
影响因子：
5.2
作者：
Du, Bin;Hong, Changqing;Sun, Yueqi
通讯作者：
Sun, Yueqi