Study of the processing map and hot deformation behavior of a Cu-bearing 317LN austenitic stainless steel-猫眼课题宝

含铜317LN奥氏体不锈钢加工图及热变形行为研究

DOI：

10.1016/j.matdes.2015.08.011

发表时间：

2015-12

期刊：

Materials & Design

影响因子：

8.4

通讯作者：

中科院分区：

材料科学1区

文献类型：

作者：

Xi Tong;Yang Chunguang;Shahzad M. Babar;Yang Ke

The hot-working behavior of a Cu-bearing 317LN austenitic stainless steel (317LN–Cu) was investigated in the 950–1150 °C temperature and 0.01–10 s− 1strain rate range, respectively. The effects of different deformation parameters and optimum hot-working window were respectively characterized through analyzing flow stress curves, constitutive equations, processing maps and microstructures. The critical strain for dynamic recrystallization (DRX) was determined by the inflection point onθ-σand −∂θ/∂σ-σcurves. The peak stress was found to increase with decrease in temperature and increase in strain rate. Typical signs of DRX over a wide range of temperatures and strain rates were observed on the flow stress curves. The power dissipation maps in the strain range of 0.1–0.4 were basically similar, indicating the insignificant effect of strain on the power dissipation maps of 317LN–Cu. However, the instability maps showed strong strain sensitivity with increasing strain, which was attributed to the flow localization. The optimum hot-working window for 317LN–Cu was obtained in the temperature range 1100–1120 °C and strain rate range 0.01–0.018 s− 1, with a peak efficiency of 38%. Microstructural analysis revealed fine and homogenized recrystallized grains in this domain.