Effect of martensitic phase transformation on the ductility of polycrystalline YCu
Effect of martensitic phase transformation on the ductility of polycrystalline YCu
复制标题
马氏体相变对多晶YCu延展性的影响
DOI：
10.1016/j.scriptamat.2011.07.030
复制
发表时间：
2011
影响因子：
6
通讯作者：
Skrotzki
中科院分区：
文献类型：
--
作者：
Oertel;Schaarschuch;Freudenberger;Brokmeier;Skrotzki
研究了挤压多晶YCu金属间化合物在室温至77K时的拉伸变形行为。观察到立方B2向正交B27相的应力诱导马氏体转变。随着温度的降低，B27相含量的增加导致了塑性的降低。在160K左右形成热诱导马氏体，合金的脆性向延性转变。讨论了160K以上塑性较高的原因。
The tensile deformation behaviour of an extruded, polycrystalline YCu intermetallic compound was investigated from room temperature down to 77K. A stress-induced martensitic transformation of the cubic B2 to the orthorhombic B27 phase was observed. The increasing amount of B27 phase with decreasing temperature leads to a decrease in ductility. A drastic decrease sets in at about 160K when thermally induced martensite is formed, characterizing the brittle-to-ductile transition of YCu. Reasons for the relatively high ductility above 160K are discussed.
登录
查看更多内容
FeAl 的室温机械行为：化学计量、环境和硼添加的影响
DOI：
--
发表时间：
1998
期刊：
影响因子：
--
作者：
J. Cohron;Y. Lin;R. Zee;E. George
通讯作者：
E. George
RCu 金属间化合物的结构不稳定性
DOI：
--
发表时间：
1989
期刊：
影响因子：
--
作者：
M. Ibarra;T. Chien;A. Pavlovic
通讯作者：
A. Pavlovic
超纯铌单晶循环变形中流动应力的温度和应变率依赖性
DOI：
--
发表时间：
1983
期刊：
影响因子：
--
作者：
F. Ackermann;H. Mughrabi;A. Seeger
通讯作者：
A. Seeger
扭转变形 NiAl 中的晶粒细化和织构形成
DOI：
--
发表时间：
2007
期刊：
影响因子：
--
作者：
B. Klöden;E. Rybacki;C. Oertel;W. Skrotzki
通讯作者：
W. Skrotzki