The preparation of mesoporous SnO2 nanotubes by carbon nanofibers template and their lithium storage properties
The preparation of mesoporous SnO2 nanotubes by carbon nanofibers template and their lithium storage properties
复制标题
碳纳米纤维模板制备介孔SnO2纳米管及其储锂性能
DOI：
10.1016/j.electacta.2013.03.036
复制
发表时间：
2013-05
影响因子：
6.6
通讯作者：
Ben Q. Li
中科院分区：
文献类型：
--
作者：
Shujiang Ding;Zhenglong Yang;Wei Yu;Ben Q. Li
以碳纤维为模板，通过简单的溶液法制备了介孔SnO2纳米管，然后在800℃下焙烧2小时。用扫描电子显微镜、透射电子显微镜、X射线衍射仪、热重分析和氮气吸附等手段对纳米管进行了表征。通过循环伏安(CV)和恒流充放电电压测试，研究了其作为锂离子电池负极的电化学性能。由于其独特的结构(介孔壁、内部孔洞和开放端)，所得到的介孔SnO2纳米管在400mAg−1的高电流密度下表现出高达50次循环的585mAhg−1的可逆容量。
Mesoporous SnO2nanotubes are prepared by templating against carbon fibers through a facile solution approach followed by calcination at 800°C for 2h. The nanotubes are characterized by means of scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), thermogravimetric analysis (TGA) and nitrogen adsorption. The electrochemical performances as the anodes of lithium-ions batteries are studied by the cyclic voltammogram (CV) and galvanostatic discharge–charge voltage tests. Because of its unique structure (the mesoporous wall, internal void and open ends), the as-obtained mesoporous SnO2nanotubes demonstrate a reversible capacity of 585mAhg−1up to 50 cycles at a high current density of 400mAg−1.
登录
查看更多内容
影响因子：
56.9
作者：
Idota, Y;Kubota, T;Miyasaka, T
通讯作者：
Miyasaka, T
影响因子：
5.4
作者：
N. Du;Hui Zhang;Bindi Chen;Xiangyang Ma;Xiaohua Huang;J. Tu;Deren Yang
通讯作者：
N. Du;Hui Zhang;Bindi Chen;Xiangyang Ma;Xiaohua Huang;J. Tu;Deren Yang
影响因子：
29.4
作者：
Liu, ZQ;Zhang, DH;Zhou, CW
通讯作者：
Zhou, CW
影响因子：
8.6
作者：
Huang, J;Matsunaga, N;Kunitake, T
通讯作者：
Kunitake, T
影响因子：
6.7
作者：
Ping Wu;N. Du;Hui Zhang;Jingxue Yu;Y. Qi;Deren Yang
通讯作者：
Ping Wu;N. Du;Hui Zhang;Jingxue Yu;Y. Qi;Deren Yang