Crevice corrosion of copper for radioactive waste packaging material in simulated groundwater
Crevice corrosion of copper for radioactive waste packaging material in simulated groundwater
复制标题
放射性废包装材料铜在模拟地下水中的缝隙腐蚀
DOI：
10.1179/1743278215y.0000000026
复制
发表时间：
2016-01
期刊：
影响因子：
--
通讯作者：
Xiaolu Pang
中科院分区：
文献类型：
--
作者：
Qiufa Xu;Kewei Gao;Quanlin Liu;Xiaolu Pang
本文所述的调查是为了弄清高放废铜容器的腐蚀行为。在模拟中国西北部地下水特征的溶液中，研究了氧、氯离子和硫酸盐离子对铜缝隙腐蚀的影响。结果表明，氧、氯离子和硫酸盐离子对缝隙腐蚀有促进作用。氯离子在铜的缝隙腐蚀机理中起重要作用，而硫酸盐离子对该机理没有影响。
The investigation described here was conducted to clarify the corrosion behaviour of high level radioactive waste containers made of copper. The influences of oxygen, chloride ion and sulphate ion on copper crevice corrosion were studied in solutions simulating groundwater characteristic of northwest China. The results showed that oxygen, chloride ion and sulphate ion promote crevice corrosion. Chloride ion was found to play a significant role in the crevice corrosion mechanism in copper, but sulphate ion had no effect on the mechanism.
登录
查看更多内容
影响因子：
6.6
作者：
C. T. Lee;Z. Qin;M. Odziemkowski;D. Shoesmith
通讯作者：
C. T. Lee;Z. Qin;M. Odziemkowski;D. Shoesmith
影响因子：
8.3
作者：
J. Duthil;G. Mankowski;A. Giusti
通讯作者：
J. Duthil;G. Mankowski;A. Giusti
DOI：
--
发表时间：
2012
期刊：
--
影响因子：
--
作者：
Fraser King;C. Lilja;Svensk Kärnbränslehantering;K. Pedersen
通讯作者：
Fraser King;C. Lilja;Svensk Kärnbränslehantering;K. Pedersen
影响因子：
8.3
作者：
Palit, A;Pehkonen, SO
通讯作者：
Pehkonen, SO
影响因子：
3.1
作者：
Feron, Damien;Crusset, Didier;Gras, Jean-Marie
通讯作者：
Gras, Jean-Marie