Annealing twins and stacking faults in niobium
Annealing twins and stacking faults in niobium
复制标题
铌中的退火孪晶和堆垛层错
DOI：
10.1016/0001-6160(61)90126-2
复制
发表时间：
1961
期刊：
影响因子：
--
通讯作者：
R. Segall
中科院分区：
文献类型：
--
作者：
R. Segall
对铌中的层错和退火孪晶进行了观察。结果表明，孪晶平面为（310），孪晶轴<310>。在与退火孪晶相同的条件下，经常观察到层错。通过电子显微镜和选定区域衍射对断层的详细研究表明，断层一般不位于{211}平面上，尽管有些断层确实具有这种定向。(M.C.G.)
Observations were made of stacking faults and annealing twins in niobium. It is shown that the twin plane is (310), the twin axis being <310>. Stacking faults were frequently observed under the same conditions as annealing twins. Detailed study of the faults by electron microscopy and selected area diffraction showed that the faults did not in general lie on {211} planes although some of the faults did have this orientation. (M.C.G.)