Compatibility of tritium permeation barrier coatings with ceramic breeder pebbles
Compatibility of tritium permeation barrier coatings with ceramic breeder pebbles
复制标题
氚渗透阻挡涂层与陶瓷增殖卵石的相容性
DOI：
10.1016/j.corsci.2021.109288
复制
发表时间：
2021
影响因子：
8.3
通讯作者：
Knitter Regina
中科院分区：
文献类型：
--
作者：
Chikada Takumi;Kolb Matthias H.H.;Fujita Hikari;Nakamura Kazuki;Kimura Keisuke;Rasinski Marcin;Hishinuma Yoshimitsu;Mukai Keisuke;Knitter Regina
具有氚渗透屏障的低活化铁素体/马氏体钢F82H样品与陶瓷增殖石接触，在550°C和700°C下在吹扫气体下退火32天。在550℃下，cr2o3形成的F82H快速反应形成三层，纯铁投影随着退火时间的延长而增大。O和Li的扩散动力学符合菲克第一扩散定律。er2o3涂层不与鹅卵石发生反应，但由于氧气通过涂层扩散而变质。体系中的杂质浓度和涂层厚度影响着固体增殖层环境下涂层的相容性。
Reduced activation ferritic/martensitic steel F82H samples with tritium permeation barriers were annealed in contact with ceramic breeder pebbles at 550 °C and 700 °C for up to 32 days under purge gas. Cr2O3-formed F82H rapidly reacted to form three layers at 550 °C, and pure Fe projections grew with annealing time. Diffusion kinetics of O and Li were well fitted with Fick’s first law of diffusion. Er2O3coatings did not react with the pebbles, but deteriorated by oxygen diffusion through the coatings. The impurity concentrations in the system and the coating thickness affect the coating compatibility in solid breeder blanket environments.
登录
查看更多内容
影响因子：
0.9
作者：
J. Konys;A. Aiello;G. Benamati;L. Giancarli
通讯作者：
J. Konys;A. Aiello;G. Benamati;L. Giancarli
聚变反应堆陶瓷涂层
DOI：
10.1016/b978-0-12-803581-8.11674-1
发表时间：
2020
期刊：
--
影响因子：
--
作者：
T. Chikada
通讯作者：
T. Chikada
评估 EUROFER 和陶瓷增殖剂之间在疲劳寿命方面的化学相容性
影响因子：
1.7
作者：
J. Aktaa;M. Walter;E. Gaisina;M. Kolb;R. Knitter
通讯作者：
R. Knitter
过量Li和Li4SiO4的Li2TiO3中Li质量损失的水蒸气浓度依赖性和温度依赖性
影响因子：
1.7
作者：
Motoki Shimozori;K. Katayama;T. Hoshino;Hiroki Ushida;Ryotaro Yamamoto;S. Fukada
通讯作者：
S. Fukada
影响因子：
1.7
作者：
Kashimura, Hideaki;Nishikawa, Masabumi;Hoshino, Tsuyoshi
通讯作者：
Hoshino, Tsuyoshi