Novel fabrication of net-like and flake-like Fe doped TiO2 thin films
Novel fabrication of net-like and flake-like Fe doped TiO2 thin films
复制标题
网状和片状 Fe 掺杂 TiO2 薄膜的新颖制备
DOI：
10.1016/j.apsusc.2011.06.083
复制
发表时间：
2011-09
影响因子：
6.7
通讯作者：
Feng, Jiayou
中科院分区：
文献类型：
--
作者：
Ren, Fujian;He, Kai;Ling, Yunhan;Feng, Jiayou
采用微弧氧化法对钛板进行微弧氧化处理，并对制备的微弧氧化- tio2薄膜进行化学处理，成功制备了不同Fe掺杂浓度的网状和片状tio2薄膜。研究发现，随着K4(FeCN)6·3H2O前驱体浓度的增加，Fe离子容易引入mao - tio2样品中，Fe的含量决定了化学处理后tio2薄膜的形貌；当铁含量较低时，表面形貌呈网状，当铁含量超过1.7%时，表面形貌呈片状。紫外可见光谱测试表明，新形貌的Fe离子掺杂tio2薄膜的吸收边有明显的红移。
New morphologies of net-like and flake-like TiO2thin films with different concentrations of Fe dopant were successfully fabricated by micro-arc oxidation (MAO) process of Ti plates and a subsequent chemical treatment of the as-prepared MAO-TiO2thin films. It was found that Fe ions can be easily introduced into the MAO-TiO2samples with the increase concentration of K4(FeCN)6·3H2O precursor, and the amount of Fe determined the morphologies of TiO2thin films after chemical treatment; net-like morphology was observed with low Fe dopant, while it transformed to a flake-like one when Fe exceeds 1.7at.%. UV–vis spectroscopy test showed that the absorption edge of the Fe ions doped TiO2thin films with new morphologies has an obvious red shift.
登录
查看更多内容
影响因子：
6.9
作者：
J. F. Li;L. Wan;Jiayou Feng
通讯作者：
J. F. Li;L. Wan;Jiayou Feng
影响因子：
3
作者：
Yang, Yang;Wang, Haiying;Wang, Ce
通讯作者：
Wang, Ce
影响因子：
6.7
作者：
Daqing Wei;Yu Zhou;Chunhui Yang
通讯作者：
Daqing Wei;Yu Zhou;Chunhui Yang
DOI：
10.1016/j.mseb.2007.02.014
发表时间：
2007-05
影响因子：
3.6
作者：
L. Wan;Jiahao Li;Jiesi Feng;Wei Sun;Zongqing Mao
通讯作者：
L. Wan;Jiahao Li;Jiesi Feng;Wei Sun;Zongqing Mao
影响因子：
8.4
作者：
Han, Chi-Hwan;Hong, Dae-Woong;Singh, Krishan C.
通讯作者：
Singh, Krishan C.