Template-based growth of TiO 2 nanorods by sol-gel process
Template-based growth of TiO 2 nanorods by sol-gel process
复制标题
溶胶-凝胶法基于模板的TiO 2 纳米棒生长
DOI：
10.15407/spqeo10.01.036
复制
发表时间：
2007
期刊：
影响因子：
--
通讯作者：
S. Mirdamadi
中科院分区：
文献类型：
--
作者：
A. Sadeghzadeh‐Attar;M. S. Ghamsari;F. Hajiesmaeilbaigi;S. Mirdamadi
本文采用溶胶-凝胶-模板法制备了二氧化钛纳米棒。用傅里叶变换红外光谱对所制备的溶胶进行了表征，并用X射线衍射仪和扫描电子显微镜对所得纳米棒进行了表征。扫描电子显微镜照片显示，二氧化钛纳米棒的直径约为100-200 nm，长度为几微米。X射线衍射结果表明，在400~700oC温度下热处理2小时后，二氧化钛纳米棒以锐钛矿相和金红石相的形式析出。
In this paper, the preparation of TiO2 nanorods by sol-gel-template process has been considered. The prepared sols were characterized by using FTIR spectroscopy, and the obtained nanorods were characterized by X-ray diffraction and SEM microscopy. SEM images show that TiO2 nanorods with uniform diameter of about 100-200 nm and a length of several micrometers. The results of XRD indicated that the TiO2 nanorods were crystallized in the anatase and rutile phases after annealing to 400-700 oC up to 2 hours.
影响因子：
6.7
作者：
Miao, L;Tanemura, S;Tanemura, M
通讯作者：
Tanemura, M
影响因子：
15
作者：
Wu, YY;Yang, PD
通讯作者：
Yang, PD