Experimental investigation of phase equilibria in the Fe-Nb-Si ternary system
Experimental investigation of phase equilibria in the Fe-Nb-Si ternary system
复制标题
Fe-Nb-Si三元体系相平衡的实验研究
DOI：
10.1016/j.jallcom.2014.03.167
复制
发表时间：
2014-08
影响因子：
6.2
通讯作者：
Wang, Cuiping
中科院分区：
文献类型：
--
作者：
Zheng, Jianping;Hu, Hongfa;Liu, Xingjun;Wang, Cuiping
用电子探针（EPMA）、背散射电子能谱（BSE）、X射线衍射（XRD）和差示扫描量热法（DSC）研究了Fe-Nb-Si三元系的相平衡。本研究测定了Fe-Nb-Si三元系在1200 °C、1100 °C和1000 °C的三个等温截面，确认了六种三元化合物。实验结果表明，Si在ε NbFe 2和μFeNb相中有较大的固溶度。新测定的Fe-Nb-Si系相平衡将为硅钢的开发提供有用的信息。
The phase equilibria of the Fe–Nb–Si ternary system were investigated by electron probe microanalyzer (EPMA), back scattered electron (BSE), X-ray diffraction (XRD) and differential scanning calorimetry (DSC) on the equilibrated alloys. In this study, three isothermal sections of the Fe–Nb–Si ternary system at 1200 °C, 1100 °C and 1000 °C were respectively determined and six ternary compounds were confirmed. The obtained experimental results show that there are large solubilities of Si in the εNbFe2and μFeNb phases. The newly determined phase equilibria of the Fe–Nb–Si system will provide useful information for silicon steels development.
登录
查看更多内容
影响因子：
6.3
作者：
Jahazi, M;Eghbali, B
通讯作者：
Eghbali, B
DOI：
10.1007/s11661-001-0133-7
发表时间：
2001-05
期刊：
Metallurgical and Materials Transactions A
影响因子：
--
作者：
S. S. Campos-S.;H. Kestenbach;Eduardo Morales
通讯作者：
S. S. Campos-S.;H. Kestenbach;Eduardo Morales
影响因子：
2.7
作者：
C. Bolfarini;M. Silva;A. Jorge;C. S. Kiminami;W. Botta
通讯作者：
C. Bolfarini;M. Silva;A. Jorge;C. S. Kiminami;W. Botta
影响因子：
6.3
作者：
S. Sankaran;V. Sarma;V. Kaushik;K. A. Padmanabhan
通讯作者：
S. Sankaran;V. Sarma;V. Kaushik;K. A. Padmanabhan
DOI：
10.1016/0022-5088(82)90038-8
发表时间：
1982-09
期刊：
Journal of The Less Common Metals
影响因子：
--
作者：
B. Malaman;J. Steinmetz;G. Venturini;B. Roques
通讯作者：
B. Malaman;J. Steinmetz;G. Venturini;B. Roques