Formation and oxidation resistance of germanium modified silicide coating on Nb based in situ composites
Formation and oxidation resistance of germanium modified silicide coating on Nb based in situ composites
复制标题
铌基原位复合材料上锗改性硅化物涂层的形成及其抗氧化性能
DOI：
10.1016/j.corsci.2013.11.029
复制
发表时间：
2014-03
影响因子：
8.3
通讯作者：
Chungen Zhou
中科院分区：
文献类型：
--
作者：
Wan Wang;Bifei Yuan;Chungen Zhou
采用Si-Ge共沉积法，在Nb-Si基合金上于1300 °C下沉积10 h，制备了Ge改性的硅化物涂层。共沉积用包粉由16 Si-8 Ge-5 NaF-71 Al 2 O3（重量%）组成。观察到涂层由外层和过渡层组成。在1250 °C氧化100 h后，衬底和Ge改性硅化物涂层的质量增益分别为190.08和5.42 mg cm-2。该涂层能有效地防止基体氧化。良好的抗氧化性归因于玻璃态GeO 2和SiO2的形成。
Ge-modified silicide coating was prepared on the Nb–Si based alloy by Si–Ge co-deposition at 1300 °C for 10 h. The pack powder for co-deposition consisted of 16Si–8Ge–5NaF–71Al2O3(wt.%). It is observed that the coating is composed of an outer layer and a transitional layer. The mass gain of substrate and Ge-modified silicide coating are 190.08 and 5.42 mg cm−2after oxidation at 1250 °C for 100 h, respectively. The coating can prevent substrate from oxidizing efficiently. The good oxidation resistance is attributed to the formation of glassy GeO2and SiO2.
登录
查看更多内容
DOI：
--
发表时间：
2007
期刊：
The Chinese Journal of Nonferrous Metals
影响因子：
--
作者：
Jiang Yuan-yuan
通讯作者：
Jiang Yuan-yuan
DOI：
10.1016/0921-5093(95)03342-4
发表时间：
1995-02
影响因子：
6.4
作者：
B. Cockeram;R. Rapp
通讯作者：
B. Cockeram;R. Rapp
影响因子：
4.4
作者：
Geng, Jie;Tsakiropoulos, Panos
通讯作者：
Tsakiropoulos, Panos
影响因子：
6.7
作者：
Yan-qiang Qiao;Xiping Guo
通讯作者：
Yan-qiang Qiao;Xiping Guo
影响因子：
1.2
作者：
M. Fukumoto;Y. Matsumura;S. Hayashi;T. Narita;Kazusi Sakamoto;A. Kasama;R. Tanaka
通讯作者：
M. Fukumoto;Y. Matsumura;S. Hayashi;T. Narita;Kazusi Sakamoto;A. Kasama;R. Tanaka