Oxidation properties of II–VI compound surfaces studied by low‐energy electron‐loss spectroscopy and 21 eV photoemission spectroscopy
Oxidation properties of II–VI compound surfaces studied by low‐energy electron‐loss spectroscopy and 21 eV photoemission spectroscopy
复制标题
DOI：
10.1116/1.570593
复制
发表时间：
1980-09
期刊：
影响因子：
--
通讯作者：
A. Ebina;K. Asano;Y. Suda;T. Takahaski
中科院分区：
文献类型：
--
作者：
A. Ebina;K. Asano;Y. Suda;T. Takahaski
Oxidation properties of ZnSe, ZnTe, CdSe, and CdTe surfaces were studied. The following combinations of experimental techniques were used: electron‐energy‐loss spectroscopy on vacuum‐cleaved ZnSe(110) surfaces and on Ar+ bombarded‐annealed surfaces of ZnSe, ZnTe, CdSe, and CdTe. Photoemission spectroscopy also was used on a vacuum cleaved ZnTe(110) surface. The oxygen uptake is very slow with exposures to molecular oxygen. Thus oxide overlayers were prepared by an electron‐beam irradiation technique which greatly enhanced the oxygen uptakes. Changes in loss spectrum detected on oxidation of CdTe can be explained by formation of TeO2. For the case of ZnTe, the shifted Te 4d loss due to TeO2 appears at the oxygen coverage, ϑ, of about 0.5 of a monolayer, and losses characterizing formation of ZnO are seen at ϑ≳1. The oxide overlayer on ZnTe is composed of TeO2 and ZnO and, in addition, an unidentified complex oxide for the heavily oxidized surface. On further oxygen exposures and beam irridation of this oxi...