Emergence of superconductivity at 45 K by lanthanum and phosphorus co-doping of CaFe₂As₂.
Emergence of superconductivity at 45 K by lanthanum and phosphorus co-doping of CaFe₂As₂.
复制标题
DOI：
10.1038/srep01478
复制
发表时间：
2013
影响因子：
4.6
通讯作者：
Nohara, Minoru
中科院分区：
文献类型：
--
作者：
Kudo, Kazutaka;Iba, Keita;Takasuga, Masaya;Kitahama, Yutaka;Matsumura, Jun-ichi;Danura, Masataka;Nogami, Yoshio;Nohara, Minoru
La-P共掺杂CaFe_2As_2在45 K下具有超导电性。 这一超导转变温度高于Ba 1 − xKxFe 2As 2的38 K转变，这是迄今为止在122个相中发现的最高值。 在Ca 1 − xLaxFe 2（As 1 −yPy）2中，在0.12 ≤ x ≤ 0.18和y = 0.06处观察到具有显著屏蔽体积分数的超导性。本系统的超导相似乎不邻近反铁磁相。
Co-doping of lanthanum and phosphorus in CaFe2As2 induces superconductivity at 45 K. This superconducting transition temperature is higher than the 38 K transition in Ba1−xKxFe2As2, which is the maximum found thus far among the 122 phases. Superconductivity with a substantial shielding volume fraction was observed at 0.12 ≤ x ≤ 0.18 and y = 0.06 in Ca1−xLaxFe2(As1−yPy)2. The superconducting phase of the present system seems to be not adjacent to an antiferromagnetic phase.
登录
查看更多内容
影响因子：
1.8
作者：
Ren, Zhi-An;Yang, Jie;Zhao, Zhong-Xian
通讯作者：
Zhao, Zhong-Xian
BaFe2As2单晶中Ni掺杂诱导的超导
影响因子：
3.3
作者：
Li, L. J.;Luo, Y. K.;Xu, Z. A.
通讯作者：
Xu, Z. A.
影响因子：
3.5
作者：
Ren Zhi-An;Lu Wei;Zhao Zhong-Xian
通讯作者：
Zhao Zhong-Xian
影响因子：
3.7
作者：
Muraba, Yoshinori;Matsuishi, Satoru;Hosono, Hideo
通讯作者：
Hosono, Hideo
硒化铁超导体中压力驱动的量子临界
影响因子：
8.6
作者：
Guo, Jing;Chen, Xiao-Jia;Zhao, Zhongxian
通讯作者：
Zhao, Zhongxian