X-ray and magnetic investigations of the high-temperature phase in the Co-rich CoV alloy system
X-ray and magnetic investigations of the high-temperature phase in the Co-rich CoV alloy system
复制标题
富钴 CoV 合金系统中高温相的 X 射线和磁学研究
DOI：
10.1002/pssa.2210330222
复制
发表时间：
1976
期刊：
影响因子：
--
通讯作者：
M. Yamamoto
中科院分区：
文献类型：
--
作者：
Y. Aoki;M. Yamamoto
对含V高达30.1 at%的fcc CoV合金进行了x射线和磁性研究。x射线测量表明，在整个组成范围内，晶格参数不服从维加德定律。晶格参数的组成依赖性可以与磁矩有关。合金的饱和矩和居里点随V含量的增加而减小，在% V时，合金在23附近由铁磁性向顺磁性转变。
X-ray and magnetic studies have been carried out for the f.c.c. CoV alloys containing V up to 30.1 at%. The X-ray measurements showed that the lattice parameter does not obey Vegard's law in the whole composition range observed in this work. The composition dependence of the lattice parameter can be related to the magnetic moment. The saturation moment and the Curie point decrease with increasing V content, and the alloy shows a transition from ferromagnetism to paramagnetism near 23 at% V. The magnetic behaviour of these alloys is discussed in connection with the magnetic properties of the ordered hexagonal VCo3 compound.
Es wurden rontgenographische und magnetische Untersuchungen fur die kubisch-flachenzentrierten CoV-Legierungen mit bis zu 30,1 At% V durchgefuhrt. Die rontgenographischen Messungen zeigten, das die gemessenen Gitterkonstanten im gesamten untersuchten Zusammensetzungsbereich von der Vegardschen Regel abweichen, was mit einer Abhangigkeit vom Sattigungsmoment zusammenhangt. Das Sattigungsmoment und der Curie-Punkt nehmen mit zunehmender V-Konzentration ab, und die Legierung zeigt einen Ubergang vom Ferromagnetismus zum Paramagnetismus bei etwa 23 At% V. Das magnetische Verhalten dieser Legierungen wird im Zusammenhang mit den magnetischen Eigenschaften der geordneten hexagonalen Verbindung VCo3 diskutiert.