Effect of oxygen partial pressure on temperature for onset of flash sintering 3YSZ
Effect of oxygen partial pressure on temperature for onset of flash sintering 3YSZ
复制标题
氧分压对闪速烧结3YSZ起始温度的影响
DOI：
10.1016/j.jeurceramsoc.2017.09.009
复制
发表时间：
2018-02
影响因子：
5.7
通讯作者：
Yiguang Wang
中科院分区：
文献类型：
--
作者：
Dianguang Liu;Yejie Cao;Jinling Liu;Yan Gao;Yiguang Wang
本文证明，在富氧环境中，氧分压会影响 3 mol% 氧化钇稳定氧化锆 (3YSZ) 的闪速烧结起始温度。闪速烧结实验的氧分压范围为 0.25–1 atm。结果表明，随着氧分压的增加，起始温度升高。根据电导率与温度的关系图，氧分压可能通过改变预闪蒸阶段的电导率来影响起始温度。结合质量作用定律的分析，确定电子传导也可能是闪速烧结预闪蒸阶段的一个关键参数，不包括氧空位传导。
In this paper, it is demonstrated that in an oxygen-enriched environment, the oxygen partial pressure affects the onset temperature of flash sintering of 3 mol% yttria-stabilized zirconia (3YSZ). Flash sintering experiments were performed with oxygen partial pressures in the range of 0.25–1 atm. The results indicate that the onset temperature increased by increasing oxygen partial pressure. According to the plots of the conductivity as a function of temperature, the oxygen partial pressure might affect the onset temperature, by changing the conductivity in the pre-flash stage. Combined to the analysis of the law of mass action, it was established that electron conduction might also represent a critical parameter during the pre-flash stage of flash sintering, excluding the oxygen vacancy conduction.
登录
查看更多内容
致密氧化锆陶瓷中电场引起的非线性导电行为
影响因子：
10.9
作者：
Gao Yan;Liu Fangzhou;Liu Dianguang;Liu Jinling;Wang Yiguang;An Linan
通讯作者：
An Linan
影响因子：
3.9
作者：
J. Francis;R. Raj
通讯作者：
J. Francis;R. Raj
影响因子：
5.7
作者：
R. Muccillo;E. Muccillo;M. Kleitz
通讯作者：
R. Muccillo;E. Muccillo;M. Kleitz
影响因子：
5.7
作者：
Kalvis Terauds;J. Lebrun;Hyun Hwi Lee;T. Jeon;Sang-Hyeon Lee;J. Je;R. Raj
通讯作者：
Kalvis Terauds;J. Lebrun;Hyun Hwi Lee;T. Jeon;Sang-Hyeon Lee;J. Je;R. Raj
影响因子：
3.9
作者：
Raj, Rishi;Cologna, Marco;Francis, John S. C.
通讯作者：
Francis, John S. C.