对 10 摩尔% NaBr 的 NaCl-NaBr 合金单晶进行了拉伸测试。 1 摩尔% NaBr 晶体具有延展性，但 5 摩尔% 和 10 摩尔% NaBr 晶体没有观察到延展性。添加 0.5 摩尔% NaBr 似乎会导致软化，这可能是由于清除作用。随着 NaBr 的加入，显微硬度持续增加至 10 摩尔%，这可能是由于溶质原子的聚集所致。在甲醇中测试的晶体具有较低的屈服应力并且更具延展性。
Single crystals of NaCl‐NaBr alloys to 10‐mole % NaBr were tested in tension. Crystals to 1‐mole % NaBr were ductile but no ductility was observed with 5‐ and 10‐mole % NaBr crystals. Addition of 0.5‐mole % NaBr appeared to cause softening, perhaps due to a scavenging effect. Microhardness showed a continuous increase with NaBr to 10 mole %, perhaps due to clustering of the solute atoms. Crystals tested in methyl alcohol had lower yield stresses and were more ductile.